摘要：本课题主要是关于一种新型强酸性阳离子交换树脂及其环保型制备方法方面的研究。该树脂以同时带有环氧基团和双键的油性单体为原料，以二乙烯基单体为交联剂，通过自由基引发的悬浮聚合制备出的带有环氧基团的均匀珠粒并进一步与带有活泼氢的氨基磺酸盐反应而制得。本研究制备的强酸性阳离子交换树脂为粒径范围为0.50～1.00mm的黄色球形颗粒，其磺酸基团的含量为17.60～20.27%，离子交换容量为2.01～2.61meq/g。20471
关键词：强酸性阳离子交换树脂；氨基磺酸盐；粒径；离子交换容量；磺酸基团含量
Study of amino sulfonate functionalized St/DVB ball
Abstract: This paper is mainly about the study on a new type of strong acidic cation exchange resin and its preparation method of environmental protection type.At the same time the resin with epoxy groups and double bonds of the oilymonomer as raw material, with two vinyl monomer as crosslinking agent,suspension caused by free radical polymerization of epoxy groups was prepared with homogeneous beads and further with a lively amino sulfonatereaction of hydrogen produced. The research on the preparation of strong acidic cation exchange resin as the particle size in the range of 0.5 ~ 1.0mm yellowspHerical particles, the content of sulfonic acid group was 17.60 ~ 20.27%, the ion exchange capacity of 2.01 ~ 2.61meq/g.
Key Words：Strong acid cation exchange resin；amino sulfonic acid；particle size；ion exchange capacity；sulfonic group content
目录
1 绪论 1
1.1 离子交换树脂的概述 1
1.2 阳离子交换树脂的概述 3
1.3 强酸型阳离子交换树脂交换树脂的应用与发展 4
1.4 阳离子交换树脂的合成工业的综述 5
1.5 悬浮聚合的概述 5
1.6 GMA的概述 6
1.7 本研究的内容及意义 7
2 实验 8
2.1原料和仪器 8
2.2 GMA/DVB球的聚合原理和磺化原理 8
2.2.1 悬浮聚合原理 8
2.2.2 磺化原理 10
2.3 强酸型阳离子交换树脂的合成制备工艺 10
2.4 GMA/DVB球以及强酸型阳离子交换树脂的性能测定 12
2.4.1 粒径测定 12
2.4.2 硫含量的测定 13
2.4.3 磺酸基团含量的确定 14
2.4.4 离子交换容量的测定 14
2.4.5 机械强度的测定 14
2.4.6 环氧值的测定 15
2.4.7 红外光谱的测定 15
3. 结果与讨论 17
3.1 GMA/DVB球和强酸型离子交换树脂的红外表征 17
3.2 悬浮聚合的合成工艺条件研究 18
3.2.1 制备工艺条件对GMA/DVB球的粒径的影响 18
3.2.2 制备工艺条件对GMA/DVB球环氧值的影响 20
3.3 磺化工艺条件的研究 24
3.3.1 溶胀剂种类对强酸型阳离子交换树脂性能的影响 25
3.3.2 pH对强酸型阳离子交换树脂性能的影响 26
3.3.3 反应温度对强酸型阳离子交换树脂性能的影响 27
3.3.4 反应时间对强酸型阳离子交换树脂性能的影响 28
4. 研究结论 29
展望 30
致谢 31
参考文献 32
1 绪论
一直以来，离子交换树脂的研究都是一个重要的问题。多年以来，科学家们在这个问题上做了很多很多的研究，也取得了不错的成果。 St/DVB球的氨基磺酸盐功能化研究:http://www.youerw.com/cailiao/lunwen_12254.html