摘要：目前，经过等径角挤压（ECAP）的铸造镁合金的性能已被广泛研究，但对于低周疲劳性能的研究甚少。对此，本文主要研究经过ECAP后，AZ31镁合金的低周疲劳性能的改变。通过对AZ31镁合金的等径角压挤，得到实验所需的试样。随后，在应变控制条件下进行疲劳实验。同时，观察ECAP处理对试样疲劳性能的影响。20801
实验结果：经ECAP处理：①细化了AZ31镁合金的晶粒，降低了静态力学性能；②提升了AZ31镁合金的塑性；③提升了AZ31镁合金的低周疲劳性能。
关键词：AZ31 等径角挤压 塑性 低周疲劳性能
毕业论文设计说明书（论文）外文摘要
Title Low-cycle fatigue behavior of micro grained AZ31 magnesium alloy
Abstract
Currently, properties of cast magnesium alloys through equal-channel-angular pressing (ECAP) have been widely studied, but studies focusing on low-cycle fatigue-property are rare. In this paper, the change of the low cycle fatigue properties of AZ31 magnesium alloy after ECAP will be mainly studied. By ECAP to AZ31 magnesium alloy, samples will be obtained. Afterwards, fatigue experiment will be conducted under the control of strain. Meanwhile, observation of the influence on fatigue-property after ECAP will be made.
Experimental results indicates that: After ECAP: ① Grain size of AZ31 magnesium alloy has been refined, static mechanical properties have been reduced. ② Plastic property of AZ31 magnesium alloy has been enhanced. ③ Low-cycle fatigue-property of AZ31 magnesium alloy has been advanced.
Keywords AZ31 equal-channel-angular pressing plastic property low-cycle fatigue-property
目 次
1 绪论 1
1.1 前言 1
1.2 镁合金的特点及应用 1
1.3 等径角挤压（ECAP） 2
1.3.1 模具结构 2
1.3.2 挤压路径 2
1.3.3 挤压道次 3
1.4 等径角挤压对AZ31镁合金的影响 4
1.4.1 晶粒尺寸对AZ31镁合金的影响 4
1.4.2 织构对AZ31镁合金的影响 5
1.5 AZ31镁合金的低周疲劳行为 6
1.6 研究内容及研究意义 6
2 材料及实验方法 7
2.1 实验方案思路 7
2.2 实验材料 7
2.3 等径角挤压变形（ECAP）实验 7
2.4 冰冷实验 8
2.5 静态力学实验 9
2.6 低周疲劳实验 9
2.7 微观组织观察 10
3 实验结果与分析 11
3.1 金相组织观察 11
3.2 静态力学性能分析 11
3.3 循环应力相应行为分析 13
3.4 应力幅曲线分析 15
3.5 疲劳寿命曲线分析 16
3.6 塑性应变幅曲线分析 17
3.7 SEM的观察与分析 18
结 论 20
致 谢 21
参考文献22
1 绪论
1.1 前言
在现下的商业领域中，AZ31变形镁合金被广泛使用，占据了很大的市场份额，是应用最为广泛的变形镁合金。在室温条件下，AZ31变形镁合金在强度、延展性以及抗大气腐蚀能力方面都有优异的表现。与其他合金相比，AZ31变形镁合金又有着造价不高的特点。由于以上优点，在航天、航空、计算机、汽车、通讯和家电等领域之中，AZ31变形镁合金都被广泛使用，并占据一席之地。 微米晶AZ31镁合金低周疲劳行为研究:http://www.youerw.com/cailiao/lunwen_12712.html