摘要 以煤沥青基中间相沥青作为前驱体进行静电纺丝制备碳纤文是目前研究的热门，中间相沥青作为煤沥青的一种深度开发产物，正越来越多的受到人们的广泛关注，我国是煤炭储量和产量大国，煤沥青作为煤炭炼焦的产物，其产量也是逐年递增，丰富的原料来源使得煤沥青的深度开发和再加工产业兴起，中间相沥青的制备方法也将对煤沥青产业产生巨大的影响。本文采用反应釜对煤焦油沥青进行热处理，通过测定产物的结焦值，软化点和偏光显微镜形貌，研究了不同热处理工艺对煤沥青合成中间向沥青的性能的影响。
关键词：中间相沥青；热聚合；
Abstract
Mesomorphic phase coal tar pitch-based precursor which used to prepare for electro-spinning is a favorite point among scientists. Mesomorphic phase CTP, depth developed from coal, has draws a lot of attention. China is abundant for storage and production in coal, the production of CTP, witch as produced from coal, is increasing year by year, resourceful for CTP draws the development of depth processing. The methods of mesomorphic phase CTP will have the huge effect of the industry. Our research used the reaction still to make a thermal treatment with CTP，by determining the softening point, coked value and POM (polarizing microscope ) scanning to research the effect ion of the properties of mesomorphic phased CTP.
Keywords: Mesomorphic phased CTP; thermal polymerization
目录
1.绪论 3
1.1煤沥青的概述 3
1.1.1煤沥青的基本组成 2
1.1.2煤沥青的基本结构 3
1.2中间相沥青 3
1.2.1煤沥青基中间相沥青形成机理研究 4
1.2.2中间相沥青的性质和结构 4
1.2.3中间相沥青的应用 4
1.3课题研究目的 5
1.4课题研究意义 6
1.5研究内容 6
1.6研究目标 7
2.实验部分 8
2.1实验主要原料 8
2.2实验仪器与设备 8
2.3试样制备工序 8
2.4直接热缩聚法制备中间相沥青的研究 9
2.4.1引言 9
2.4.2实验部分 9
2.5催化缩聚法制备中间相沥青工艺研究 9
2.5.1引言 9
2.5.2实验部分 10
2.6分析仪器的表征及方法 10
2.6.1软化点 10
2.6.2结焦值 11
2.6.3偏光显微镜光学分析 11
3结果与讨论 11
3.1 实验结果 11
3.1.1结焦值测定结果 11
3.1.2 偏光显微镜测定中间相含量 14
3.1.3 软化点测定结果 14
4结果分析 15
参考文献 16,3746
1.绪论
1.1煤沥青的概述
煤沥青是一种组成与结构都非常复杂的混合物，它的确切成份尚不清楚，但其基本组成单元基本是多环、稠环芳烃以及衍生物[1]。由于煤沥青化学组成以及结构的复杂性，所以常常用溶剂组分分析法来表征它的特性[2]。由于煤沥青基本是以芳香族为主的结构复杂的高分子化合物混合体，常含有不溶于溶剂的碳质成分，根据其组成物质在不同溶剂中的溶解度不同，于是可将煤沥青分离为若干具有相似物理、化学性能的芳香族化合物，习惯上把溶剂分离法也称作为族组成分析法。煤沥青是高度缩合后的碳一杂环化合物以及其缩合后产物的复杂多相系统。因为这些缩合产物的芳构化程度、组成、性质、分子结构等都不尽相同，因此在不同溶剂中的溶解度也不尽相同。对这些缩合产物进行研究，并选择溶解能力不同的溶剂对煤沥青进行溶剂抽提，就可把沥青复杂系统分成不同的族组分，也叫族组成分析法。了解煤沥青的不同组分分布以及各组分不同的物理和化学性质即可在一定程度上了解煤沥青的组成情况，更好地对煤沥青加以分析。 热聚合工艺对煤沥青性能的影响（绪论+实验）:http://www.youerw.com/cailiao/lunwen_131.html