摘要本论文所研究的是选择具被10-9米颗粒的立方相序介孔二氧化硅MCM-48作为实验合成的模板原材料，设计、制备具有一定颗粒形貌、颗粒尺寸分布的包埋铁酸钴的磁性介孔材料，研究了该材料对稀土矿渣滤液中的稀土金属离子铈离子的吸附性能，本论文讨论了在形同实验条件下吸附时间、pH、投加量的吸附试验研究。用紫外分光光度仪测量试验数据，最后对实验数据结果进行了结果分析。实验结果表明在室温条件下吸附50mg/l的硝酸铈溶液其最佳吸附条件为投加量50mg、吸附时间2h、pH4左右。21969
关键词 硝酸铈 吸附 磁性介孔
毕业论文设计说明书（论文）外文摘要
Title：Ordered mesoporous materials for magnetic rare earth waste adsorption behavior of the filtrate
Abstract：The subject has selected sequence cubic nanoparticles mesoporous silica MCM-48 as the template material, design, mesoporous materials prepared having a magnetic particle morphology, particle size distribution of cobalt ferrite embedded studied the material adsorption of rare earth rare earth metal ions in the filtrate slag cerium ions, the paper discusses, pH, dosage experimental study of adsorption at adsorption time just like the experimental conditions. The spectrophotometric measurement test data, and the results were analyzed. Experimental results show that the adsorption of 50mg / l of cerium nitrate solution the optimum conditions for the adsorption dosage 50mg, adsorption time 2h, about pH4 at room temperature.
Key words Cerium nitrate adsorption Magnetic mesoporous
目次
1、绪论 1
1.1稀土元素 1
1.1.1稀土元素化学性质 1
1.1.2稀土元素物理性质 1
1.2金属铈元素 2
1.3硝酸铈 2
1.4水中原子序数较大的金属去除方法 2
1.4.1化学沉淀法 3
1.4.2离子交换法 3
1.4.3氧化还原法 3
1.4.4溶剂萃取法 4
1.4.5膜分离法 4
1.4.6吸附法 4
1.5介孔材料 5
2.实验部分 6
2.1实验仪器 6
2.2铁酸钴的制取： 6
2.3磁性介孔材料的制备 11
2.4磁性介孔材料对硝酸铈溶液的吸附行为 13
2.4.1配制pH=2的硝酸 13
2.4.2配制500ml的100mg/l硝酸铈溶液 13
2.4.3溶液稀释 13
2.4.4配制偶氮胂Ⅲ 13
2.4.5配制标准曲线 14
2.4.6测量标准曲线吸光度 14
2.5实验数据 15
2.5.1相同实验条件下不同投加量对吸附效率的影响 15
2.5.2相同实验条件下吸附效率之时间的影响 17
2.5.3相同实验条件下不同溶液吸附效率之pH的影响 19
结论 22
致谢 23
参考文献 24
1、绪论
1.1稀土元素
元素周期表中质子数57 到71 的15种镧系金属元素属于稀土元素，还有两种金属元素钪（Sc） 和钇（Y），他们的化学性质与原子序数57~71的原子相似，也属于稀土元素，所以稀土元素一共有17个。由于这17种元素原子的电子层结构相似，所以有着类似的物理化学性质，它们在矿藏中大多是共生的。但它们并不是所有的性质都类似，由于不同的离子半径，所以它们也有一些不同的理化。稀土元素的共性是：①它们的原子结构相似；②离子半径相近（REE3+离子半径1.06×10-10m~0.84×10-10m，Y3+为0.89×10-10m）；③它们在自然界密切共生。 磁性有序介孔材料对稀土废渣滤液的吸附行为:http://www.youerw.com/cailiao/lunwen_14418.html