摘要由于现有的可注射水凝胶存在力学性能不足等缺点，本课题通过使用乳化交联法制作壳聚糖微球，并使之与水凝胶复合，制作出一种壳聚糖微球填充的可注射水凝胶细胞支架材料，发展出一种具有良好力学性能的可注射复合支架材料。
通过采用乳化交联法，并合理地控制实验条件，最终制得的壳聚糖微球球形完整，粒度均匀。而后将壳聚糖微球与氧化硫酸软骨素-羧甲基壳聚糖水凝胶进行复合，相较于空白水凝胶，采用上述步骤得到包埋了一定量壳聚糖微球的复合支架材料具有溶胀度小，体外降解速度慢，力学性能好等优点。27156
关键词 乳化交联法 壳聚糖微球 OCS-CMCS水凝胶 复合支架材料
毕业论文设计说明书外文摘要
Title Preparation of injectable microspheres composite polysaccharide hydrogels
Abstract
As the existing injectable hydrogel exists deficiencies of mechanical properties and other shortcomings, we prepared chitosan microspheres through using crosslinking emulsion methods, aligning them with the hydrogel composite, we can obtain one type of injectable hydrogel filled with chitosan microspheres, which have good mechanical properties.
By using emulsion crosslinking method and reasonable control of the experimental conditions, the obtained chitosan microspheres were spherical shape with a regular surface and uniform size. Then we composite chitosan microspheres with OCS-CMCS hydrogel, compared with blank hydrogel, by using the above procedures, the obtained composite scaffold material embedded a certain amount of chitosan microspheres has a small degree of swelling, slow vitro degradation, good mechanical performance.
Keywords emulsification crosslinking method chitosan microspheres OCS-CMCS hydrogels composite scaffolds
目 次
1 绪论 1
1.1 课题背景 1
1.2 水凝胶、微球与支架材料 3
1.3 课题的提出 5
2 材料与方法 7
2.1 主要试剂和仪器 7
2.2 壳聚糖微球的制备 7
2.3 OCS-CMCS水凝胶的制备 7
2.4 微球-水凝胶复合支架的制备 8
2.5 溶胀性能测试 8
2.6 微观形貌观察 9
2.7 体外降解实验 9
2.8 力学性能测试 10
3 结果与讨论 11
3.1 壳聚糖微球制备过程中的影响因素 11
3.2 壳聚糖微球微观形貌 11
3.3 水凝胶的微观形貌 12
3.4 溶胀性能 13
3.5 体外降解 14
3.6 力学性能 16
结论 18
致谢 19
参考文献 20
1 绪论
1.1 课题背景
关节的软骨损伤是骨科临床工作中的常见难题。因软骨本身缺乏血液供应，仅靠关节滑液提供大部分营养。因此软骨一旦受损，自身很难进行修复[ ]。在目前的实际应用中，常用的软骨损伤修复方法包含了软骨下骨钻孔技术、磨削成形术、微骨折技术、自体或异体软骨细胞植入技术等[ ]。但是在软骨损伤修复的实际应用中，上述方法却存在着缺点和不足。而近年来在生物医学领域得到迅速发展的骨组织工程，则给软骨损伤修复提供了一种新的思路和方法[ ]。 可注射型微球复合多聚糖水凝胶的制备:http://www.youerw.com/cailiao/lunwen_21570.html