摘要：本文通过对加入了Cr、Mo、Ti等元素的NiAl合金进行高温氧化实验来讨论Cr、Mo、Ti等元素对此合金的高温氧化性能的影响。试验中将运用XRD对试样表面氧化物进行材料组成物相的分析，运用SEM对试样进行表面形貌的分析。结果表明：对NiAl合金进行高温氧化处理会形成氧化膜；对XRD结果和能谱分析结果进行分析可知氧化膜的成分主要为Al2O3、Cr2O3、TiO2；合金表面的氧化膜对样品有有效的保护作用，基本保持了不错的高温抗氧化性。本课题将为NiAl合金的实际应用提供一定的实验基础和理论依据。33911
毕业论文关键词：NiAl；高温氧化性能；氧化膜 ；高温抗氧化
The effect of Cr, Mo, Ti elements on high temperature oxidation behavior of NiAl-based alloy
Abstract:This txet discusses the influence of NiAl-based alloyby joining elements
such as Cr, Mo, Ti alloy on high temperature oxidation performance experiments.Material composition was analyzed by means of XRD test specimen phase analysis and sample the surface morphology was analyzed by SEM.Through the analysis of test results and discussion got:NiAl alloy oxide film was formed on high temperature oxidation treatment,the results of XRD and energy spectrum analysis showed that the major ingredients of oxide film was Al2O3,Cr2O3 , TiO2.sample was protected effectively and maintained a good high temperature oxidation resistance of the conclusion because of alloy on the surface of the oxide film.This experiment will provide experimental foundation and theoretical basis for practical application of NiAl and alloy。
Key words: NiAl ；High temperature oxidation performance Oxide film High temperature oxidation resistance
目录
1第一章 绪论 1
1.1 高温合金 1
1.1.1 概述 1
1.1.2 性能及强化方法 2
1.1.3 分类 3
1.1.4 用途 4
1.2 NiAl基金属间化合物 4
1.2.1 概述 4
1.2.2 性能 5
1.2.3 NiAl的制备 5
1.3 高温氧化 7
1.3.1 概述 7
1.3.2机理 7
1.4 NiAl合金的高温氧化行为 7
1.5 本课题的目的和意义 8
2试验方法与过程 8
2.1 试验合金制备 8
2.2 实验方法： 8
2.3所需设备 10
2.4 分析方法 13
3 实验结果与讨论 14
3.1 XRD图谱分析 14
图3.1 900℃氧化10h的NiAl 合金表面氧化物的XRD测试分析结果 14
用jade软件对所得谱图进行分析简要步骤如下 14
3.2 SEM表面形貌分析 15
3.3 讨论 26
4 结论 27
参考文献 28
致谢 29
1 绪论
1.1 高温合金
1.1.1 概述
高温合金是以铁、钴、镍作为基体，能在600℃以上的温度和一定压力条件下适应不同环境短时或长时使用的金属材料。上世纪40年代英、美等西方国家就已经开始大力研究高温合金并成功制出了镍基的高温材料，前苏联也不甘落后在50年代前后研制成功这一性能优异的材料，最具典型的就是镍铬奥氏体耐热钢16-25-6和前苏联研制的Эн481奥氏体耐热钢。不过他们的使用温度并没有超过700~750℃。 CrMoTi等元素对NiAl合金高温氧化行为的影响:http://www.youerw.com/cailiao/lunwen_31229.html