摘要中碳调质钢含碳量为0.25%-0.5%，其圆棒锻造过程中易产生夹渣等缺陷。本课题对超声无损检测的发展状况做了分析，对比不同类型超声C扫描。采用手动超声A扫描初步确定工件有无缺陷以及大体位置、性质，并检测人工缺陷试样缺陷，绘制当量曲线图。在A扫描的前提下，运用水浸式超声C扫描对圆棒中存在的缺陷进行更加准确的分析。实验过程通过探头的合理选择、检测参数的调整改善超声C扫描结果，根据C扫描结果分析工件缺陷，从而保证工件质量。67494
毕业论文关键词 中碳调质钢 超声A扫描 超声C扫描 人工缺陷
毕业设计说明书（论文）外文摘要
Title The defect of medium carbon quenched and tempered steel's axle forming and welding parts ultrasonic C scanning NDT test research Abstract
The carbon of quality score in medium carbon quenched and tempered steel is 0.25%-0.5% , the shaft is easy to produce the defects such as slag inclusion, porosity in the forging process.In the topic, We analyzed the situation on the development of ultrasonic nondestructive testing,and Compared of the different types of ultrasonic C scanning. Use manual ultrasonic a-scan preliminary determine the workpiece defect,the location and nature generally,and test the artificial defect to draw equivalent diagram . Under this premise, using water immersion ultrasonic C scan to get more accurate analysis. Through the reasonable choice of probe and adjust test parameters to Optimize C scan results. According to the C scan results, analysis of workpiece defects to ensure the quality of workpiece.
Keywords medium carbon quenched and tempered steel ultrasonic A scan ultrasonic C scan artificial defect
目录
1 绪论 1
1.1 中碳调质钢的特性及应用 1
1.2超声无损检测的发展状况 2
1.3 超声C扫描分类及对比 3
1.4 课题研究目的及内容 4
2 中碳调质钢圆棒手动超声A扫描试验 4
2.1 试验材料、设备与方案 5
2.2 探头的选择和性能分析 6
2.3 人工试样缺陷的制备 7
2.4 缺陷波形的采集 8
2.5 试验数据整理及结果分析 9
2.6 本章小结 ..10
3 中碳调质钢圆棒水浸式超声C扫描试验 11
3.1 试验材料、设备与方案 11
3.2 探头和水距的选择 14
3.3 检测参数的设定… 16
3.3 试验结果分析 17
3.4 本章小结 18
结论 19
致 谢 20
参考文献 21
1 绪论
随着科学技术在工业中的运用逐步深入，工业无损检测技术也成为工业发展的一个重要保障。超声波无损检测作为无损检测技术的一部分，起着极其重要的作用。超声波C扫描装置可以直接显示在缺陷部分的任何横截面图案，可以直观的看到缺陷形状，确定缺陷的大小，继而综合判定缺陷的性质。这对缺陷检查人员判断缺陷的尺寸和性质是非常有帮助的[1]。超声Ｃ扫描检测中，将探头垂直于工件，对距离探头一定距离的工件内部切面进行检测分析，最终形成二维图像。它具有灵敏度高、成像直观、自动化程度高等优点，在无损检测领域得到广泛应用[2]。 中碳调质钢轴类成形与焊接件缺陷超声C扫描无损检测试验研究:http://www.youerw.com/cailiao/lunwen_75717.html