摘要：本文使用了一种新的残余应力的测量方法——比容差法。分别从冷镦、冷轧、热轧还有温降工艺出发，通过实验将比容差法和钻孔法进行三维残余应力的比对，结果表明，比容差法可以精确定量的测量不同金属处理工艺下材料内部产生的三维残余应力，并且与盲孔法实验结果进行比较，有较好的一致性。接下来对金属处理工艺后的材料进行了材料残余应力分布的测量与分析，得出比容差法可以精确测量得出材料内部残余应力的分布情况，并得出其分布规律。71931

毕业论文关键词：残余应力、金属压力加工、比容差法、小孔法

Measurement and Analysis of Residual Stress Distribution in Materials

Abstract：

In this paper, a new residual stress measurement method is used。 The results show that the tolerance method can be used to quantitatively measure different metals, and the results show that the method can be used to measure the temperature of the different metals by means of the method of tolerance, cold rolling, hot rolling and temperature drop。 The three - dimensional residual stress produced by the material under the treatment process is compared with that of the blind hole method, and the consistency is better。 Then, the measurement and analysis of the residual stress distribution of the material after the metal treatment process are carried out。 The distribution of the residual stress in the material can be accurately measured and the distribution law is obtained。

Key Words:

Residual stress, metal pressure processing, specific tolerance method, small hole method

目录

1 绪论 4

1。1 残余应力 4

1。2 材料残余应力的测量方法 4

1。2。1钻孔法测量残余应力 5

1。2。2 盲孔分析 5

1。2。3 切条法 7

1。2。4 磁测法 7

1。2。5 X射线衍射法 8

1。2。6 超声波法 8

1。2。7 中子衍射法 8

1。3 比容差法 9

1。4 论文的目的和意义 9

2 实验方法以及过程 10

2。1 实验设备 10

2。2 塑性变形实验 12

2。3 冷却实验 13

2。4 比容差法实验 13

2。5 钻孔法实验 14

3 比容差法测量材料残余应力分布 15

3。1 比容差法的可行性验证 15

3。1。1 比容差法原理 15

3。1。2 比容差法对纯铝试样的残余应力测量 16

3。1。3 钻孔法对比容差法的实验验证 17

3。2 纯铝高度方向上的残余应力测量 18

3。2。1 纯铝冷镦后的比容差法测量分析 18

3。2。2 钻孔法验证 20

3。3 复合热轧板层深方向上的残余应力测量 20

3。3。1复合热轧板比容差法测量分析 22 材料残余应力分布的测量与分析:http://www.youerw.com/cailiao/lunwen_81714.html