摘要采用金相显微镜对 7A55 铝合金铸锭原始组织和中厚板固溶后的再结晶组织进 行观察，采用扫描电镜（SEM）对 7A55 铝合金铸锭样品，轧板和固溶后的板材进 行第二相的观察，采用透射电镜（TEM）对 7A55 铝合金-T7751 时效态样品进行观 察。采用硬度，电导率和拉伸测试等试验方法研究 7A55 铝合金厚板回归再时效后 组织与性能沿厚度方向的关系。研究结果表明：再结晶分数从板材和铸锭的表层到 心部依次降低，粗大第二相的尺寸从板材和铸锭的表层到心部逐渐增大，电导率和 强度在板材心部最高。79803

毕业论文关键词：7A55 铝合金；中厚板；大尺寸铸锭；不均匀性

Abstract The original structure of 7A55 aluminum alloy ingot and recrystallization microstructure of the plate after solid solution were observed by the optical microscope。 The second phase observations of ingot, rolling plate and the plate after solid solution were achieved by scanning electron microscopy (SEM)。 The precipitations under T7751 treatment were observed by transmission electron microscopy (TEM)。 The relationship between microstructure and properties of 7A55 aluminum alloy thick plate after the regression and re aging was studied by means of hardness, electrical conductivity and tensile test。 The results showed that: the recrystallization fraction of the plate and ingot reduced from surface to centre。The coarse second phase particles size of the plate and ingot gradually increased from surface to center。 The conductivity and strength in plate center was the highest。

Keywords：7A55 aluminum alloy; plate; large size ingot; inhomogeneity

目 录

第一章 文献综述 1

1。1  铝合金在航空工业中的应用 1

1。2  国外航天航空铝合金的发展 2

1。3 中国航空航天铝合金的发展 5

1。4 AlZnMgCu 合金(板材)组织和性能的不均匀性 6

1。4。1 AlZnMgCu 合金铸锭的不均匀性 6

1。4。2 AlZnMgCu 合金热轧板材的不均匀性 8

1。5 本文的研究背景 14

1。5。1 7A55 铝合金的用途 14

1。5。2 本文的研究意义及内容 15

第二章 实验材料和方法 17

2。1  实验用料 17

2。2  实验方案 17

2。3  组织分析 17

2。3。1 金相组织分析 17

2。3。2 扫描电镜（SEM）观察 18

2。3。3 透射电镜（TEM）组织分析 18

2。4  性能测试与分析 18

2。4。1 硬度 18

2。4。2 电导率 19

2。4。3 室温拉伸性能 19

2。5  主要实验设备 19

第三章 7A55 铝合金(中)厚板组织与性能的不均匀性 20

3。1  均匀化态铸锭组织的厚向不均匀性 20

3。2 轧制态粗大第二相的厚向不均匀性 7A55高强铝合金大尺寸铸锭和板材的组织及性能不均匀性:http://www.youerw.com/cailiao/lunwen_92442.html