电铸法制备仿形砂轮工艺研究

摘要电铸法是一种操作方便，成本较低，易实现自动化、机械化的工艺方法。随着时代的发展，电铸法越来越频繁的用于仿形砂轮的制备。本文采用3因素3水平的正交实验，围绕电铸温度，上砂时间，上砂电流密度等因素进行电铸仿形砂轮工艺的研究。测试了砂轮的表面露出高度，发现当上砂时间为240min，温度为40～46℃，电流密度为1A/dm2时制备的砂轮表面露出高度最小。通过高温循环氧化实验，发现当上砂时间为360min，温度为54～60℃，上砂电流密度为1。5A/dm2时砂轮的抗高温循环氧化能力最强。通过静态腐蚀浸泡实验，发现当上砂电流密度为1A/dm2，温度为40～46℃，上砂时间为300min时砂轮的耐腐蚀性最好。81138

毕业论文关键词电铸法仿形砂轮正交实验

毕业设计说明书外文摘要

Title Research on preparation of profiled grinding wheel by electroforming

Abstract Electroforming is a process method, which is convenience, less expensive, easy to achieve automated and mechanized。 With the development of the times, electroforming is more and more frequent used on the preparation of profiled grinding wheel。 With three factors and three levels orthogonal experiments, this study focuses on electroforming temperature, time on the sand and the current density of electroforming to improve profiled grinding wheel。 It found that when the sand time 240 min, at 40～46 ℃, with the current density on 1A/dm2 the exposed surface would become least。 High temperature cyclic oxidation experiment found that when the sand time is 360 min, at 54～60 ℃ with the current density of the sand on 1。5A/dm2 high temperature oxidation resistance would be best 。 Static corrosion immersion test found that when the current density of the sand is 1A/dm2 ,at 40～46 ℃ with 300 min sand time corrosion resistance of the wheel would be best。

Keywords Electroforming; Profiled grinding wheel; Orthogonal experiment

1 引言 1

1。1 磨削加工方法 1

1。1。1 砂纸打磨 1

1。1。2 珠光处理 1

1。1。3 液体平滑 1

1。1。4 机械磨削 1

1．2 仿形砂轮简介 2

1。2。1 磨料的选择 2

1。2。2 结合剂的选择 2

1．3 电铸法 3

1。3。1 电铸分类及原理 3

1。3。2 铸件基体 4

1。3。3 电铸电源 4

1．4 研究意义及内容 4

1。4。1 研究意义 4

1。4。2 主要内容 4

2 电铸材料及方法 6

2．1 电铸仿形砂轮实验材料 6

2．2 电铸仿形砂轮预实验 6

2。2。1 电铸仿形砂轮预实验因素与水平 6

2。2。2 基体及磨粒的前期处理 7

2。2。3 电铸过程电铸法制备仿形砂轮工艺研究:http://www.youerw.com/cailiao/lunwen_94590.html