摘要：本文以异佛尔酮二异氰酸酯（IPDI），甲基丙烯酸羟乙酯（HEMA），丙烯酸正丁酯（BA），甲基丙烯酸（MAA），甲基丙烯酸十二氟庚酯为原材料合成了紫外光固化水性聚氨酯丙烯酸酯树脂。通过红外光谱的测定，证明了固化涂膜主要成分为水性含氟聚氨酯丙烯酸酯树脂且已固化完全。通过对比实验得出: MAA的含量在6 %时，光引发剂的用量为3 %时，涂膜具有合适的固化时间，较好的铅笔硬度和柔韧性；当固化时间为6 s时，涂膜完全固化。84622

毕业论文关键词：水性聚氨酯丙烯酸酯；光引发剂；甲基丙烯酸酯

Properties of UV-curable Waterborne 

Polyurethane Acrylate Coating

Abstract: In this paper, UV-curable waterborne polyurethane acrylate resin have been synthesized with isophorone diisocyanate (IPDI), 2-hydroxyethyl methacrylate (HEMA), butyl acrylate (BA), methacrylic acid (MAA), methacrylate perfluoro heptyl as raw material。 It was proved that the product was water soluble polyurethane acrylate and its film had been cured by the infrared spectrum。 By contrasting experiments, it was confirmed that when the content of MAA was 6 % and the content of photoinitiator was 3 %, the film had a good comprehensive performance with high pencil hardness and flexibility; and when the curing time was 6 s, the coating was cured completely。

Key Words: Waterborne polyurethane acrylate; Photoinitiater; Methyl methacrylate 

目    录

摘  要 1

引  言 1

1 实验部分 3

  1。1 仪器与试剂 3

  1。2 原料处理 4

  1。3 实验方法 4

  1。4 分析测试方法 6

2 结果与讨论 7

  2。1 红外光谱分析 7

  2。2 甲基丙烯酸用量对固化膜性能的影响 7

  2。3 引发剂用量对固化时间的影响 8

  2。4 光引发剂含量对固化涂膜硬度的影响 9

  2。5 光引发剂含量对固化涂膜柔韧性的影响 10

  2。6 辐射时间对涂膜性能的影响 10

3 结  论 11

参考文献 12

致  谢 14

紫外光固化水性聚氨酯丙烯酸酯涂料的性能研究

引 言紫外光（UV）固化技术是一种快速得到固化漆膜的方法[1]。紫外光固化的速率非常快，固化一般的涂膜只需要几秒钟[2]；由于生产效率很高，可以进行大规模的生产[3]；而且其固化的温度要求比较低[4,5]，能够节约资源。更为重要的是紫外光固化技术是一项绿色高效的材料合成新技术[6,7]，符合人们日益关注的绿色环保的要求。传统的UV固化涂料是不溶于水的油溶性涂料，其原料大都较贵，为了降低成本，一般会在制备时添加大量溶剂，使体系不能完全固化，从而使涂膜的性能受到影响。有机溶剂毒性大、易挥发、极易造成环境污染。另外，油溶性的紫外光固化体系主要是由光引发剂、参加反应的齐聚物和改变工艺粘稠度的活性稀释剂构成[8]。活性稀释剂在固化后有很浓烈的味道，对皮肤有一定的影响[9]，其残留物也会对涂膜的后期物理性能产生影响，对产品的安全和卫生产生负面的影响。为了绿色健康，水性紫外光固化涂料越来越受到欢迎。论文网 紫外光固化水性聚氨酯丙烯酸酯涂料的性能研究:http://www.youerw.com/huaxue/lunwen_100591.html