摘 要混合电容器是一种介于超级电容器和电池之间的一种新型储能装置,与传统的双电层电容器相比,它具有更高的能量密度;与电池相比,具有更高的功率密度。混合电容器在移动通讯,信息技术等方面具有极其重要的应用前景。86260
实验中通过复合共沉积方法制备了掺杂了WO3的PbO2电极材料,将其做成混合电容器的工作电极,WO3-PbO2和C分别作为混合电容器的负极和正极,组装成WO3-PbO2/C 混合电容器。通过测试其循环伏安和充放电等性能,发现其具有良好的比电容值,结果显示,放电电流为5 mA/cm2时,充放电测得的电容器比电容值为69。9 F/g,并且拥有长久的循环寿命。
毕业论文关键词:混合电容器;二氧化铅;三氧化钨;复合共沉积
Abastract A novel hybrid capacitor is a new energy storage means interposed between a supercapacitor and a battery , as compared with a conventional electric double layer capacitor having higher energy density; Compared with batteries, having higher power density。 Hybrid capacitors have very important applications in mobilecommunications, information technology, etc。
Experiment by co-deposition method for preparing a compound doped PbO2 electrode material of WO3, which is made of a hybrid capacitor working electrode, WO3-PbO2 and C were used as the negative electrode and a positive electrode of a hybrid capacitor, assembled into WO3-PbO2/C Mixed capacitors。 Tested by cyclic voltammetry and charge-discharge performance, it was found to have a good ratio of capacitance values, The results showed that when the discharge current is 5 mA/cm2, the capacitance value of capacitor were measured more than 69。9 F/g ,and has a long cycle life。
Keywords:Hybrid capacitor;Lead dioxide;WO3;Composite codeposition
目 录
第一章 绪论 1
1。1 纳米WO3的性质与应用 1
1。1。2 纳米WO3的应用研究 1
1。1。3 纳米WO3的制备方法 3
1。2 PbO2电极材料的概述 4
1。2。1 PbO2电极材料的研究现状及发展 4
1。2。2 PbO2电极的电化学性质 5
1。3 混合电容器简介及储能原理 6
1。3。1 双电层电容器 6
1。3。2 法拉第电容器 6
1。3。3 混合电容器 7
1。4 复合共沉积方法概述 7
1。4。1 复合共沉积法 7
1。4。2 复合共沉积法的原理 8
1。4。3 复合共沉积过程的影响因素 9
1。5 论文选题目的、意义和研究内容 10
1。5。1 选题目的和意义 10
1。5。2 研究内容 10
第二章 实验仪器、药品和研究方法 11
2。1 主要实验仪器 11
2。2 主要实验试剂 11
2。3研究方法 WO3-PbO2/C混合电容器的组装及性能研究:http://www.youerw.com/huaxue/lunwen_102535.html