石墨烯填充橡胶复合材料的制备及性能研究

摘要本论文通过添加改性剂聚乙烯吡咯烷酮（PVP）制备了具有良好水溶性的改性石墨烯（PVP-GE），并将其与天然橡胶（NR）进行乳液混合，制备了PVP-GE/NR复合材料，对PVP-GE进行了表征分析，并研究了复合材料的硫化性能、拉伸性能、撕裂性能、热稳定性以及溶剂渗透性能。其结果表明：PVP的加入不影响GO的有效还原，而且改性的石墨烯可以在水中均匀分散，TG和DSC分析表明PVP与GE存在一定的相互作用，从而使得PVP-GE中PVP组分的降解得到延缓。PVP-GE的加入减慢了NR混炼胶的硫化速度，但MH-ML的增加反映出橡胶的交联密度不断增加。橡胶的拉伸强度和撕裂强度随着PVP-GE的增加逐渐提升，在3phr达到最好，M100，M300，拉伸强度，撕裂强度分别提升了412%，900%，17%，146%。此外，PVP-GE还能有效的提升NR硫化胶的热稳定性和溶剂渗透性能。19346
关键字：石墨烯，天然橡胶，机械性能，热稳定性
毕业论文设计说明书（论文）外文摘要
Title             Preparation and Properties of
           natural rubber composites filled with graphene
Abstract
This thesis by adding modified agent polyvinylpyrrolidone (PVP) was prepared with good solubility in water modified graphene (PVP - GE), and its emulsion mixed with natural rubber (NR), PVP - GE/NR composite was prepared, and analysis had been used to characterize the PVP - GE, and studied the vulcanization properties of the composite, the tensile properties, tear resistance, thermal stability and solvent permeability .The results show that the addition of PVP does not affect the effective reduction of the GO, and modification of graphene can be evenly dispersed in water, TG and DSC analysis showed that PVP with GE has certain interaction, so as to make the PVP - GE PVP component in the degradation of delay .PVP - GE's join slows down the NR mixing rubber vulcanization rate, but the increase of MH - ML reflects rubber crosslinking density increased .Rubber tensile strength and tear strength increased with the increase of PVP - GE gradually improve, achieve the best in 3 PHR, M100 approximately, M300, tensile strength, tear strength improved respectively 412%, 900%, 17%, 146%.In addition, the PVP - GE also can effectively improve thermal stability of NR vulcanizates and solvent permeability.
Key words: Graphene, natural rubber, mechanical properties, thermal stability
目录
1   绪论   1
1. 1   石墨烯结构特征和优异性能   1
1. 2   石墨烯制备方法   1
1.2.1   微机械分离法   1
1.2.2   外延生长法   1
1.2.3   氧化还原法   2
1.2.4   化学气相沉积   2
1. 3   石墨烯的改性   2
1.3.1   非共价键改性石墨烯   2
1.3.2   共价键改性石墨烯   3
1.3.3   电化学改性石墨烯   3
1.4   石墨烯在聚合物中的应用   3
1.4.1   提高热学性能   4
1.4.2   改善力学性能   4
1.4.3         提高电学性能   4
1.5        本课题的主要研究内容    5 石墨烯填充橡胶复合材料的制备及性能研究:http://www.youerw.com/huaxue/lunwen_10656.html