摘要：本文以仲钼酸铵和浓硝酸为原料，采用水热合成法制备三氧化钼纳米阵列，通过改变反应时间和马弗炉中的煅烧温度，寻找三氧化钼纳米阵列生长最佳时间和光催化效果最好的煅烧温度。在产物合成以后，采用扫描电镜（SEM）表征对晶型和晶貌进行研究，并以亚甲基蓝为目标染料，在汞灯的照射下，利用紫外分光光度计探究MoO3纳米阵列膜的光催化性能。结果表明，高压反应釜中反应16个小时，550℃煅烧2小时的MoO3纳米阵列膜对亚甲基蓝溶液的光催化降解效果最好，汞灯下照射一小时降解率可达98。8%。88653

Abstract：Based on (NH4)6Mo7O24·4H2O and HNO3,the mixed solution plays a role as precursor。MoO3 nanoparticle array can be synthesized by hydrothermal method 。By means of changing reaction time and calcine temperature,the  most suitable time for MoO3 nanoparticle array to grow and the most suitable temperature for dye to be degraded can be found。After MoO3 nanoparticle array prepared,use scanning electron microscope to research crystallization properties and crystal morphologies。Methylene bule is dye,photocatalytic performance of MoO3 nanoparticle array can be tested with the light of mercury lamp。 Experimental results show that MoO3 nanoparticle array which is produced by reacting 16h in high pressure reactor and calcine 2h in 550℃ have a best effect。After one hour, degradation rate reach up to 98。8%。源Q于D优G尔X论V文Y网wwW.yOueRw.com 原文+QQ75201`8766

毕业论文关键词：三氧化钼；水热合成法；光催化；亚甲基蓝

  Keyword:MoO3;hydrothermal method;photocatalysis;Methylene bule

目    录

1。引言 4

1。1 研究背景 4

1。2研究意义 4

1。3研究流程 4

1。3。1制备MoO3纳米阵列 4

1。3。2煅烧反应产物 4

1。3。3光催化性研究 4

1。3。4实验产物表征分析 4

1。4国内外研究现状 5

2。MoO3纳米阵列概述 5

2。1MoO3纳米阵列基本性质 5

2。2MoO3纳米阵列的光催化原理 6

3。 实验过程 7

3。1实验用品 7

3。1 。1实验试剂 7

3。1。2实验仪器 7

3。2实验过程 7

3。2。1清洗基底片 7

3。2。2制备三氧化钼纳米阵列 7

3。2。3表征分析 8

3。2。4三氧化钼纳米阵列光催化性能测试 8

3。2。5煅烧温度的选择 8

3。2。6最佳反应时间From优T尔K论M文L网wWw.YouERw.com 加QQ75201^8766 探究实验 8

4。 结果与分析 9

4。1扫描电镜结果分析 9

4。2光催化性能结果分析 11

4。2。1煅烧温度对光催化性能的影响 11

4。2。2水热反应时间对光催化性能的影响 12 MoO3光催化剂制备及性能研究:http://www.youerw.com/huaxue/lunwen_164842.html