摘要:铈锆固溶体因拥有良好的储氧性能和较高的热稳定性以及优异的低温催化性能,被用作汽车尾气净化催化剂载体,并受到广泛关注。本课题主要通过改进的Pechini方法来合成大比表面积的介孔铈锆固溶体。用非离子表面活性剂F127作为模板剂,正硅酸四乙酯和酚醛树脂分别作为无机和有机的前驱体,酚醛树脂,八水氯氧化锆和优尔水硝酸铈分别作为碳,锆和铈的来源物质。采用改进的Pechini方法是将硝酸铈和氯化氧锆同有机溶剂(柠檬酸和乙二醇)结合,形成配合物,然后与表面活性剂F127、resol以及正硅酸四乙酯结合在一起,最后通过XRD、能谱图和N2吸脱附图来表征。24608
毕业论文关键词: 铈锆固溶体;介孔材料;柠檬酸;Pechini新方法
The Controllable generation of Mesoporous Ce1-xZrxO2 Solid Solutions with Modified Pechini new approach
Abstract: Mesoporous Ce1-xZrxO2 Solid Solutions have been synthesized via modified Pechini approach by using Pluronic F127 as a template and resol, Zirconium oxychloride octahydrate and Cerium nitrate hexahydrate are as carbon, Zr and Ce sources. Moreover, phenolic resin is used as an organic precursor and prehydrolyzed TEOS is used as an inorganic precursor. The new approach named pechini is mixing basic zirconium chloride and cerous nitrate and organic solvent (citrate acid and 1,2-ethanediol) to form chelate compound. And then mix them with F127, ethanol,TEOS and phenolic resin. The samples were characterized by XRD,energy spectrum diagram and nitrogen adsorption--desorption isotherms.
Keywords: Cerium Zirconium Composite Oxide; Mesoporous Material; citric acid; Pechini new approach
目录
1绪论 5
1.1 氧化铈和氧化锆的相关介绍 5
1.1.1 关于氧化铈 5
1.1.2 关于氧化锆 5
1.1.3 铈锆复合氧化物的相关介绍 6
1.2 氧化铈锆固溶体的制备方法 6
1.2.1 共沉淀法 6
1.2.2 溶胶-凝胶法 7
1.2.3 表面活性剂模板法 7
1.2.4 PMMA模板剂法合成介孔铈锆固溶体材料 7
1.2.5 超临界干燥法 7
1.2.6 改进溶胶一凝胶法 8
1.2.7 改进的高分子凝胶法 9
1.2.8 柠檬酸溶胶凝胶法 9
1.2.9 其他方法 10
1.3 氧化铈锆固溶体的制备方法比较 10
1.4 Pechini方法简介 10
1.4.1 用改进的Pechini法制备钇铝石榴石纳米晶粉体 10
1.4.2 Pechini 法合成 BaCe0.7Zr0.2Gd0.1O3-δ质子导体 11
1.4.3 可行性分析 11
1.5 研究思路 11
2 实验部分 12
2.1 仪器与试剂 12
2.1.1 实验试剂 12
2.1.2 实验仪器 12
2.2 Pechini方法介孔氧化铈锆固溶体的制备及表征 13
2.2.1 实验原理 13
2.2.2 实验步骤 13
2.2.3 介孔氧化铈锆的表征方法 13
2.2.5 Pechini方法制备介孔氧化铈锆固溶体的实例二 17
2.2.6 Pechini方法制备介孔氧化铈锆固溶体的实例三 26
2.2.7 pechini方法制备介孔氧化铈锆固溶体的实例四 30
2.3运用改进的 Pechini方法介孔氧化铈锆固溶体的制备及表征 35
2.3.1 实验原理 35 改进的Pechini方法制备介孔氧化铈锆固溶体:http://www.youerw.com/huaxue/lunwen_18194.html