摘要：陶瓷膜在分离应用中均存在膜易受污染、通量衰减等缺点，严重影响了陶瓷膜的分离效率。通过纳米氧化物颗粒修饰改性能有效提高陶瓷膜的性能。本文采用具有高亲水性的非化学计量纳米氧化钛改性氧化铝陶瓷微滤膜，优化改性工艺参数，提高其亲水性和抗污染性能。结果表明：当涂膜时间为50s、煅烧温度为650℃时，膜的性能最好，分离效率最高，此时的渗透液和截留液的COD值分别为255。8mg/L和1156mg/L，截留率达到了77。87%，渗透液浊度为0。632NTU。91519
毕业论文关键词：非化学计量二氧化钛，膜污染，陶瓷膜，油水分离
Abstract: Membrane fouling weakens seriously the membrane’s separating performance, which can be reduced by the membrane surface modification。 The nano-metal oxide particles could effectively increase the ceramic membrane’s performance。 In the present work, the Al2O3 microfiltration membrane was modified with nano-sized non-stoichiometric TiO2-x coating prepared in N2 atmosphere。 The results show that the Al2O3 microfiltration membrane modified with the nano-sized non-stoichiometric TiO2-x, which was prepared under the coating time of 50 seconds and sintering temperature of 650℃,had better stable flux。 Using the stable oil–water emulsion as feed, the oil rejection was 77。87%。 COD values of permeate and retentate were 255。8 g/mL and 1156 g/mL, respectively。 And the turbidity of permeate was just 0。632 NTU。
Keywords: non-stoichiometric TiO2-x, membrane fouling, modification, Ceramic membrane, emulsion separation
目录
1前言 4
1。1陶瓷微滤膜 4
1。1。1陶瓷微滤膜的性质源G于J优L尔V论N文M网WwW.youeRw.com 原文+QQ75201`8766 及特点 4
1。1。2陶瓷微滤膜的现状 4
1。2氧化铝微滤膜 4
1。2。1氧化铝微滤膜的性质及特点 4
1。2。2氧化铝微滤膜的制备方法 5
1。2。3氧化铝微滤膜的影响因素 5
1。2。4氧化铝微滤膜的改性 5
1。3二氧化钛 5
1。3。1二氧化钛的性质及特点 5
1。3。2二氧化钛的制备方法 6
1。3。3二氧化钛的改性 6
1。3。4二氧化钛的表征方法 6
1。3。5二氧化钛的应用 6
1。4 本文研究内容和目的 7
2实验部分 7
2。1实验仪器和试剂 7
2。2 实验步骤 8
2。2。1膜的制备 10
2。2。2 膜的分离 10
2。2。3膜的清洗 11
2。3实验测定和分析方法 11
2。4工艺参数的选择 12
3结果与讨论 12
3。1非化学计量纳米二氧化钛的形态对负载量的影响 非化学计量纳米氧化钛改性氧化铝陶瓷微滤膜:http://www.youerw.com/huaxue/lunwen_199015.html