摘 要：本课题在凹凸棒土表面接枝PDMAEMA高分子链，考察改性凹土（PGS-g-PDMAEMA）对BSA的吸附性能。考察溶液pH、改性凹土用量以及溶液温度对吸附效果的影响。结果表明：当溶液pH值为7。4时，PGS-g-PDMAEMA对BSA的吸附量最低；随着凹土投入量的增加，纯凹土的吸附量先减小后增大，PGS-g-PDMAEMA先增大后减小。当改性凹土投入量为0。03 g时，PGS-g-PDMAEMA的吸附性能最好；随着温度的上升，吸附量也在增大。91657
毕业论文关 键 词：凹凸棒土，PDMAEMA ，吸附性能，BSA
Abstract: In this work, the PDMAEMA polymer chains were grafted on the surface of palygorskite, and the adsorption properties of modified palygorskite (PGS-g-PDMAEMA) for BSA were investigated。 The influence of pH, dosages of the PGS-g-PDMAEMA and temperature on the adsorption capacity of BSA was studied。 The results showed that when the pH was 7。4, the adsorption amount of PGS-g-PDMAEMA was the lowest。 With the increase of the dosages, the adsorption amount of the palygorskite decreased first and then increased。 When the dosage of palygorskite was 0。03 g, the adsorption property of PGS-g-PDMAEMA was best。 And the adsorption capacity increased with the increase of temperature。 源G于J优L尔V论N文M网WwW.youeRw.com 原文+QQ75201`8766
Keywords: palygorskite, PDMAEMA, adsorption, BSA
目 录
1 引言 3
1。1 凹凸棒土 3
1。2 PDMAEMA 4
1。3 吸附 5
1。4 选题的依据及研究的内容 7
2 实验部分 7
2。1 实验药品及仪器 7
2。2 牛血清蛋白（BSA）标准曲线的测定 8
2。3 改性凹土投入量不同下吸附量的测定 8
2。4 不同pH下改性凹土吸附量的测定 8
2。5 不同温度下改性凹土吸附量的测定 9
3 结果与分析 9
3。1 BSA标准曲线 9
3。2 电镜及能谱分析 10
3。3 不同凹土量下的吸附量 11
3。4 不同pH下的吸附量 12
3。5 不同温度下凹土吸附量 13
结 论 15
参 考 文 献 16
致 谢 18
1 引言
1。1 凹凸棒土
1。1。1 凹土性质来自优I尔Y论S文C网WWw.YoueRw.com 加QQ7520~18766
凹凸棒土被称作坡缕石，又叫坡缕缟石(Palygorskite)，简称凹土(PGS)[1]。其矿物成分是一种极罕的天然非金属粘土矿物，隶属海泡石族。其理想化学成分为是一种结晶的水合硅酸铝硅酸盐[2]，拥有层链状的结构，棒状、纤维状，宽50~150 nm，长500~ 5000 nm[3]，是一种纯天然的矿物纳米材料。晶体结构如图1-1所示：
图1-1晶体结构[5]
凹土具有如下几种性质[4~5]：①流变性。如图1-1所示，双链间只有氧桥键联结，联结能力弱，又由于其特殊的晶体结构和细小的晶体外形，这让其在外加压力下可以足够地分散开来，具有很好的流变性能力。②吸附性[6]。凹土的内部结构呈沸石孔道，使其拥有较大的内比表面积，另外单个的凹土晶体为细小纤维棒状，聚拢时无规则沉淀，干燥之后又会派生出次生孔隙，所以凹土就形成了巨大的比表面积。③催化性。晶体内氧桥键破裂、非等价阳离子类质同交换以及加热导致的晶体缺陷都会让坡缕石内部结构和外表出现多个碱化中心和酸化中心，这对酸碱共同催化反应有很大地帮助。④可塑性[7]。当水的质量与它自身重量相同时时，凹凸棒土会到达塑性的极限；⑤环保性好。化学惰性，无污染、绿色环保。 PDMAEMA改性凹凸棒土的吸附性能:http://www.youerw.com/huaxue/lunwen_199174.html