摘 要：本文首先利用原子转换自由基聚合法，在凹凸棒石表面接枝聚N-异丙基丙烯酰胺，制备一系列不同接枝率的有机-无机复合材料，再将其掺杂到聚偏氟乙烯基质中，通过相转化法制备混合基质超滤膜，研究共混改性剂接枝率对膜形成过程及微结构的影响规律。不同接枝率的聚N-异丙基丙烯酰胺改性凹土对膜孔径大小影响不大，纯聚偏氟乙烯膜和改性膜的平均孔径均在20nm左右。随着聚N-异丙基丙烯酰胺接枝率的增加，膜孔的数量增加，并且孔分布更加整齐均匀。92649

毕业论文关键词：凹凸棒石，聚偏氟乙烯，超滤膜，相转化法

Abstract: A thermo-responsive inorganic-organic nanofiber additive (palygorskite-g-poly(N-isopropylacrylamide), which was first fabricated via “graft from” technic, was incorporated into PVDF membrane matrix to improve the hydrophilicity。 The PVDF/PGS-g-PNIPAAM hybrid membranes was prepared via a combination of immersion precipitation (IP) and thermally induced phase separation (TIPS) process。 The influence of graft ratio on membrane structures and properties were investigated。 The results shows that The graft ratio of PGS-g-PNIPAAM  had little effect on the pore size of the membrane, and the average pore size of pure PVDF membrane and modified membrane was about 20nm。 With the increase of the graft ratio of PGS-g-PNIPAAM, the number of pores increases, and the distribution of thepore is more uniform。源F于K优B尔C论V文N网WwW.youeRw.com 原文+QQ752^018766

Keywords: palygorskite polyvinylidene fluoride, ultrafiltration membrane, phase inversion method 

目录

1。 引言··3

1。1  聚偏氟乙烯膜··3

1。2  凹凸棒黏土·4

1。3  聚偏氟乙烯·4

1。4  膜分离技术·5

2。 实验部分·6

2。1 实验试剂及仪器6

2。2  膜的制备7

2。3  膜的表征8

3。  结果与讨论··9

3。1 红外光谱分析··9

3。2 电镜分析··10

3。3 XRD的分析·11

3。4 膜孔径分析12

3。5 纯水通量··13

结 论·15

参 考 文 献··16

致 谢··18

1。 引言

1。1 聚偏氟乙烯膜

1。1。1  聚偏氟乙烯膜的分类来自优O尔P论R文T网WWw.YoueRw.com 加QQ7520`18766

聚偏氟乙烯微孔膜已经成功的被应用在过滤气体、精制有机溶剂和膜蒸馏等各个领域。

聚偏氟乙烯超滤膜早在1981年刘双进等人就以丙酮和二甲基甲酰胺作为混合溶剂并且以聚乙二醇600作为添加剂制作成了平板膜[1]。

聚偏氟乙烯共混膜对扩大膜材料具有重要意义，随着膜技术飞快发展，对膜材料的性能要求也在不断地更新提高。据报道聚砜、PN、PMMA和磺化聚芳醚砜等物质和PVDF混溶制备膜[2-4]，发现聚偏氟乙烯的结构中存在可以形成氢键的原子，聚砜中也同样存在，因此选用非质子性溶剂。

为了达到拓展聚偏氟乙烯膜的应用的目的，改善其亲水性和疏水性是一种途径。董声雄等用Tween 80的水溶液浸泡聚偏氟乙烯超滤膜并且先用化学处理使得超滤膜表面具有极性基团，再进行涂层处理，使膜具有更加稳定的亲水性[5]。 温敏性聚偏氟乙烯-凹凸棒石混合基质超滤膜的制备:http://www.youerw.com/huaxue/lunwen_200350.html