纳米凹凸棒石改性氧化铝微滤膜的油水分离性能

摘要：含油废水是一种常见的污染源，若不经过处理就直接排放，会对环境保护和生态平衡产生很大危害，因此对含油废水进行处理很重要。本文使用纳米凹凸棒石改性氧化铝微滤膜处理含油废水，考察料液温度、跨膜压差和膜面流速等操作条件对膜分离性能的影响。实验结果表明：当跨膜压差为0。15 MPa，料液温度为45 ℃时，在膜面流速为1。33m/s的条件下过滤效果较好，此时截留液的COD为1486mg/L，渗透液的COD为294。5mg/L，COD截留率达到了80。18%。当跨膜压差为0。19MPa，膜面流速为1。33 m/s，料液温度为45℃时纳米凹凸棒石改性氧化铝微滤膜的稳定渗透通量最大。93995

毕业论文关键词：含油废水，改性氧化铝微滤膜，膜分离，COD

Abstract: Oily wastewater is a common source of pollution。 If it is discharged directly without treatment, it will cause great harm to environmental protection and ecological balance。 So it is very urgent to deal with oily wastewater。 This study aimed to treat oily wastewater via the nano-attapulgite modified alumina microfiltration membrane, and investigate the effects of liquid temperature, the trans-membrane pressure and cross-flow velocity on membrane separation performance。 The experimental results showed that under the following operation conditions:△P=0。15MPa, T=45℃, and v=1。33m/s, the COD value of permeate and retentate were 294。5 mg/L and 1486 mg/L,respectively。 And rejection was 98。72 %。 When the trans-membrane pressure was 0。19MPa, the cross-flow velocity was 1。33 m/s and the feed temperature was 45℃, the nano-attapulgite modified alumina microfiltration membrane has the highest steady flux。

Keywords: oily wastewater, Modified alumina microfiltration membrane, membrane separation, COD

1 引言 4

1。1 含油废水 4

1。1。1 含油废水简介 4

1。1。2 含油废水分类 4

1。1。3 含油废水处理现状 5

1。2 膜分离技术 5

1。2。1 膜定义 5

1。2。2 微滤膜 6

1。3 本文研究目的和内容 6

2 实验部分 6

2。1 实验仪器和试剂 6

2。1。1实验试剂 6

2。1。2实验主要仪器及设备 7

2。1。3氧化铝陶瓷膜结构参数 7

2。2实验方案 7

2。2。1 纳米凹凸棒石改性氧化铝微滤膜的制备 7

2。2。2 膜微滤操作装置 8

2。3 实验数据处理方法 9

2。4 实验测定和分析方法 9

2。5 操作条件 9

3 结果与讨论 9

3。1 操作条件对膜渗透性能的影响 9

3。1。1 跨膜压差对膜渗透性能的影响 10

3。1。2 料液温度对膜渗透性能的影响 10

3。1。3 膜面流速对膜渗透性能的影响 11

3。2 操作条件对膜截留效果的影响纳米凹凸棒石改性氧化铝微滤膜的油水分离性能:http://www.youerw.com/huaxue/lunwen_201941.html