摘要:近年来用共沉淀法制备氧化钇透明陶瓷已经成为透明陶瓷工艺研究的一个热门，但是却多用静置陈化，搅拌陈化因为不可控因素太多而少有问津。本实验对共沉淀法采用搅拌陈化做出了初步的尝试。研究了在不同搅拌时间下得到的氧化钇粉体以及制成的陶瓷的性能的影响。使用硝酸铝作为烧结助剂，研究了加入硝酸铝的量对制成粉体以及陶瓷的性能的影响。26560
毕业论文关键词：透明陶瓷 氧化钇粉体 共沉淀法 搅拌陈化
Y2O3 Preparation and optical properties of transparent ceramics
Abstract: In recent years, the preparation of Y2O3 transparent ceramics by co-precipitation method has received much attention. Static aging in process of co-precipitation was often used, however, mixing aging was used less because of too many uncontrollable factors. In this thesis, we use mixing aging in process of co-precipitation method to synthesize Y2O3 transparent ceramics. One of the aims of this work is to study the influence effect on Y2O3 powder and performance of as-prepared ceramics by changing different stirring times. The adding amount of sintering additive Al (NO3)3 was optimized to study the influence of the performance for synthesized powders and ceramics.
Key word: Transparent ceramics Y2O3 Powder Co-precipitation method Mixing aging
目录
第一章 绪论.5
1.1 透明陶瓷..5
1.2 透明激光陶瓷的优点.5
1.3 氧化钇的物理化学性质..5
1.4 透明陶瓷的应用..6
1.5 共沉淀法..7
1.6 实验目的以及步骤7
第二章 样品的表征方法..8
2.1 X射线衍射分析..8
2.2 场发射扫描电镜..8
2.3 密度测定..8
2.4 透过率的测定.8
2.5 光学显微镜9
第三章 详细实验过程.9
3.1 原料9
3.2 实验仪器..9
3.3 配置溶液.10
3.3.1 取超纯水.10
3.3.2 配置沉淀剂..10
3.3.3 配置实验样品10
3.4 滴定..10
3.5 实验变量陈化时间..11
3.6 抽滤..11
3.7 煅烧..12
3.8 筛粉..12
3.9 压片..12
3.10 烧制成型13
3.11 添加烧结助剂..13
第四章 数据分析.13
4.1 陈化时间对粉体以及陶瓷性能的影响.13
4.1.1 温度..13
4.1.2 粉体形貌图..14
4.1.3 不同陈化时间的粉体的XRD结果..15
4.1.4 密度..16
4.1.5 透过率17
4.1.6 光学显微镜..18
4.2 烧结助剂对粉体性能的影响19
4.2.1 添加硝酸铝对陶瓷密度的影响.19
4.2.2 掺杂硝酸铝的粉体的XRD结果.20
4.2.3 SEM表面图像20
4.3 小结..21
第五章 结论与展望21
5.1 结论..21
5.2 不足及展望..22
参考文献23
致谢.25
第一章 绪论
1.1 透明陶瓷
1959年美国通用电气公司陶瓷学家R.L.Coble首次研制出透明Al2O3陶瓷-Lucalox，为陶瓷打开了新的应用篇章[1]。把无机物粉末烧结达到一定的透明度就成了透明陶瓷。研磨抛光后的透明陶瓷透光率大于40%，放在有字的纸上能看到纸上的文字。陶瓷材料的微观结构有一个共同的特点:含有大量细小的晶粒，晶粒之间有玻璃状物质和气孔[2]。陶瓷中的晶界、气孔和杂质会导致光线在陶瓷内散射或被吸收，以至于陶瓷不透明。透明陶瓷内气孔几乎等于零，因此能够达到玻璃一般的透明度。 氧化钇透明陶瓷的制备及其光学性能:http://www.youerw.com/huaxue/lunwen_20785.html