摘要：本文研究了溶液介质对铜表面自组装不同防变色膜的防变色效果的影响。以苯并三氮唑和十二烷基硫醇作为成膜物，通过在水溶液中加入乙醇、二乙二醇丁醚改变成膜条件，制备防变色膜。对已经附载了自组装膜的铜片进行交流阻抗和电化学极化的测试。测试发现，在未十二烷基硫醇附载的自组装膜的耐腐蚀效果要优于苯丙三氮唑，在改变了溶液介质的浓度之后，二者耐腐蚀效果相差的更加明显；在当十二烷基硫醇作为自组装膜负载在铜电极上时，乙二醇二丁醚可以起到更好的协同效果；当自组装膜为苯丙三氮唑（C6H5N3）时，改变乙二醇二丁醚的浓度的效果依然是比改变乙醇的浓度明显，但是如果和以十二烷基硫醇作为自组装膜的铜电极相比，效果不如十二烷基硫醇的效果明显。31984
毕业论文关键词：自组装膜；铜腐蚀；腐蚀抑制剂； 十二烷基硫醇；苯丙三氮唑
Effect of solution medium on anti color effect of  assembled film of copper surface
Abstract：
Dodecyl mercaptan and benzotriazole as a membrane material, by in aqueous solution added ethanol, ethylene glycol monobutyl ether changing membrane forming conditions and preparation of anti tarnishing film. For AC impedance and electrochemical polarization has been attached to the self assembled film of copper test. The effect of ratio (load test, it is found that in the absence of dodecyl mercaptan annexed the self-assembled film corrosion effect is superior to that of benzene third azole in changing the solution concentration, the two corrosion effect difference is more obvious; when dodecyl mercaptan as self assembled.
Keyword：self-assemble；copper corrosion；corrosion inhibitor；dodecyl -mercaptan  ethylene；glycol monobuty
 目  录
1 前言    1
1.1 研究背景    1
1.2自组装膜技术    2
1.3 铜的腐蚀    2
1.3.1空气腐蚀    3
1.3.2海洋腐蚀    3
1.3.3土壤腐蚀    3
1.4 目前铜的防腐蚀处理    4
1.4.1 将天然物质作为缓蚀剂    4
1.4.2 有机化合物缓蚀剂    4
1.5 十二烷基硫醇在铜电极表面自组装膜的形成以及溶液介质的影响    5
1.5.1 自组装膜的形成    5
1.5.2 溶液介质对TD成膜的影响    5
1.6 苯丙三氮唑在铜电极表面自组装膜的形成及溶液介质的影响    6
1.6.1 自组装膜的形成    6
1.6.2 溶液介质的影响    6
2 实验部分    7
2.1 实验试剂与设备    7
2.1.1实验试剂    7
2.2 实验过程    7
2.2.1乙醇溶液对铜表面苯丙三氮唑所形成自组装膜的影响    7
2.2.2二乙醇二丁醚溶液对苯丙三氮唑所形成自组装膜的影响    8
2.2.3 乙醇溶液对十二烷基硫醇所形成自组装膜的影响    8
2.2.4 二乙醇二丁醚对十二烷基硫醇所形成自组装膜的影响    8
2.3 性能表征    8
2.3.1三电极体系    8
2.3.2 交流阻抗    9
2.3.3动电位极化曲线    9
3 实验结果与讨论    10
3.1 乙醇溶液对铜表面苯丙三氮唑所形成自组装膜的影响    10
3.1.1 交流阻抗    10
3.1.2极化曲线    11
3.2乙醇溶液对十二烷基硫醇所形成的自作装膜的影响    13
3.2.1交流阻抗    13
3.2.2极化曲线    14 溶液介质对铜表面组装膜防变色效果的影响:http://www.youerw.com/huaxue/lunwen_28353.html