摘要:本论文是以硅钢级氧化镁的废弃物为原料，在不同温度时间下煅烧计算失重率。再与聚乙烯、聚丙烯复合测量其力学性能。经过多次试验，得到最佳的实验方案。实验结果表明：在650℃下煅烧5h能得到最好的失重率。然后将该条件下的产品与有机物进行不同比例的复合，测量拥有全新力学性能的复合材料。36482
毕业论文关键词: 硅钢级氧化镁；聚丙烯；聚乙烯；力学性能
Modification of magnesium oxide waste modified plastics by oriented silicon steel Study on
the properties of composite materials
Abstract: This topic is based on the silicon steel grade magnesium oxide as raw material, and the weight loss rate was calculated by calcination at different temperatures..Then measurement the mechanical properties after compound with PE or PP.After many experiments, the best experimental program was obtained.The experimental results show that the best weight loss rate of calcined 5H in 650℃.Then，compound the products with organic compound by different proportions.In the end，measure the compound material which with full new mechanical properties.
Key Word: silicon steel grade magnesium oxide;polypropylene;polyethylene;
mechanical properties
目  录
1 文献综述    1
1.1 工程塑料的发展及应用    1
1.2 聚丙烯材料的发展及应用    2
1.2.1 聚丙烯材料的发展状态    2
1.2.2 聚丙烯材料的缺点及阻燃化    3
1.3 聚乙烯材料的应用    6
1.3.1 聚乙烯材料的应用    6
1.3.2 聚乙烯材料的缺点及阻燃化    6
1.4 塑料添加剂发展    7
1.4.1 塑料添加剂的分类    7
1.4.2 塑料添加剂的发展    8
1.5 硅钢简介    8
1.5.1 硅钢用MgO的要求    9
1.5.2 硅钢用MgO废弃物的产生    9
1.5.3 硅钢用MgO废弃物回收再利用的研究意义    10
1.6 选题背景及意义    11
2 实验部分    12
2.1 实验原料及实验仪器    12
2.2 实验过程    12
2.2.1 硅钢级氧化镁的除碳实验    12
2.2.2 球磨实验    13
2.2.3 包覆实验    13
2.2.4 力学性能试验    13
2.3 性能测试    13
2.3.1 XRD测试    13
2.3.2 SEM测试    13
2.3.3 TEM测试    13
2.3.4 IR测试    14
2.3.5 力学性能测试    14
3 结果与讨论    14
3.1 实验分析    14
3.1.1废弃物结构表征（XRD）    14
3.1.2 SEM    15
3.1.3 硅钢级氧化镁的作用机理研究    16
3.2 废弃物的除碳研究    17
3.2.1 除碳失重率计算    17
3.2.2 XRD分析    17
3.3 废弃物的超细化研究    18
3.4 包覆形貌    19
3.4.1 红外光谱分析    19
3.5 力学性能研究    20
3.5.1 拉伸    20
3.5.2 硬度    20
4 结论    20
致谢    22
参考文献    23
文献综述
1.1 工程塑料的发展及应用
工程塑料主要是指能用作结构材料的热塑性塑料。工程塑料具有优良的综合性能，刚性大，蠕变小，机械强度高，耐热性好，电绝缘性好，可在较苛刻的化学、物理环境中长期使用，可替代金属作为工程结构材料使用，但价格较贵，产量较小。 取向硅钢氧化镁废弃物改性塑料复合材料及性能研究:http://www.youerw.com/huaxue/lunwen_34963.html