摘要：本课题旨在研究一种不含钴的三价铬钝化溶液，并对不含有金属钴的钝化液的性能进行研究，研究内容包括钝化膜的耐腐蚀性，钝化膜的组成，钝化工艺的参数(钝化时间、钝化温度)等，在数据分析和讨论的基础上，得出较好的钝化液配方和工艺参数。 采用合理、科学的实验方法研究钝化液组成、钝化时间及钝化温度对所形成的钝化膜性能的影响，测试不同试样表面形貌、耐腐蚀性能及膜的组成，并对各条件下所得到的数据进行分析和讨论。6670
关键词：三价铬； 钝化膜； 钴；耐蚀性
Study of trivalent chromium passivation without cobalt
Abstract: The purpose of this paper is to study a kind of trivalent chromium passivation solution not containing cobalt, and study the properties of passivation solution contains no metal cobalt, research contents include the corrosion resistance of passive films, the composition of the film, passivation process parameters (temperature, passivation passivation time), in the basis of analysis and discussion the passivation solution, and gets a better formulation and process parameters. The rational, scientific experiment method to study the effect of passivation solution, passivation time and passivation temperature on the passivation film performance, composition of the test specimens with different surface morphology, corrosion resistance and film, and the condition under which the data are analyzed and discussed.
Keywords: Trivalent chromium passivation film; corrosion resistance; cobalt;
目录
1.绪论 2
1.1 三价铬钝化工艺的现状和趋势 2
1.1.1 三价铬钝化工艺工艺的发展现状[1] 2
1.1.2三价铬钝化工艺工艺的发展趋势[2] 2
1.2 三价铬钝化现存的问题 4
1.2.1成本高问题 4
1,2.2 钝化液文护与操作要求高 5
1.2.3钝化层色泽问题 5
1.2.4 三价铬盐钝化层中出现优尔价铬的问题 5
1.3 影响三价铬钝化层耐蚀性的诸多因素 8
1.3.1 浓缩钝化剂的选择 8
1.3.2 镀锌层厚度的影响 8
1.3.3 电镀方式的影响 8
1.3.4 钝化类型 8
1.3.5 镀锌工艺的影响 9
1.3.6 不同光亮剂的影响 9
1.3.7 钝化条件的影响 9
1.3.8 钝化膜划伤的影响 10
1.3.9 滚镀锌件三价铬钝化的困难 11
2 实验部分 13
2.1课题研究内容 13
2.2实验主要仪器和材料 13
2.2.1镀锌层的制备 13
2.3实验原理 14
2.3.1 钾盐镀锌的技术原理 14
2.4钝化膜性能测定方法 17
2.4.1结合力试验 17
2.4.2耐腐蚀性能测试 17
2.4.3镀层厚度测试 18
2.4.4 极化曲线 18
2.4.5 钝化膜形貌及成分 18
2.5 工艺成分的作用和影响 18
2.5.1配方组成 18
2.5.2 本实验钝化液配方 18
2.5.3 工艺条件的影响 19
（1） pH值 19
（2）温度 19
（3）钝化时间 19
2.5.4 三价铬钝化工艺流程 19
3 实验结果及讨论 19
3.1 钝化参数对钝化膜外观和耐蚀性能的影响 19
3.2 钝化膜的形貌及成分 21
4 实验结论 26 三价铬无钴钝化研究+文献综述:http://www.youerw.com/huaxue/lunwen_4298.html