摘要：本文采用了恒电位、循环伏安和 Tafel等电化学方法研究了镁铝合金分别在中性、碱性和酸性氯化钠溶液中的阳极溶解过程。研究表明：在酸性溶液中：即使有氧化膜保护，也很容易被腐蚀，相比在中性和碱性溶液中，更容易被腐蚀；在中性溶液中：与在酸性和碱性溶液中相比，腐蚀没有在酸性溶液中剧烈，但是比在碱性溶液中剧烈。51219
毕业论文关键词：镁铝合金、pH、氯化钠、阳极溶解
Effects of pH of the anodic dissolution of magnesiumaluminum alloy in sodium chloride solutionAuthor: Yu YongchenAdviser: Li LiangAbstract: In this paper, effects of pH on the anodic dissolution of magnesiumaluminum alloy in NaCl solution were studied by using the constant potential, cyclicvoltammetry and Tafel methods. The results showed the anodic dissolution was moreeasily in acidic solution than in neutral and alkaline solutions, even though there is aprotection film on the surface of the electrode. In the neutral solution, the anodicdissolution was more severe than that in the alkaline solution, but more weak than thatin the acid solution.
keywords：magnesium alloy; pH; sodium chloride; anodic dissolution1 前言镁及其合金具有密度低，其比强度、比刚度和比弹性模量高等诸多优点，能够作为航空、航天工程材料，是最有发展前途的一种轻质材料。然而镁铝合金耐蚀性很差,在空气中会产生腐蚀[1,2,3]，使其应用受到严重制约[4]。对于铝来说，在空气中其表面也形成一层氧化膜[5,6]，通常条件下不容易腐蚀，当有侵蚀性离子，如氯离子的存在下，容易发生点腐蚀[7,8,9]。因此，镁合金的表面防护处理极为重要[10,11,12]。 由于镁铝合金中的是一种两性金属， 在酸性和碱性条件下均容易腐蚀，因此有必要研究pH 对镁铝合金阳极溶解过程的影响。本文旨在研究pH 对镁铝合金在氯化钠溶液中阳极溶解过程中的影响[13]，为防止镁铝合金在不同pH 条件下的腐蚀提供实验依据。2 实验部分本文采用三电极系统。工作电极直径为 1.6 mm 的镁铝合金(AZ31B: Mg95.451%，Al 3.19% )，源`自*优尔~文·论^文`网[www.youerw.com周围用环氧树脂密封，每次实验前只露出断面，镍片作为对电极，饱和甘汞电极作为参比电极。每次实验前，先将电极表面分别用 600目和 1500目的金相砂纸打磨，然后用蒸馏水冲洗干净。恒电位实验过后，分别用去离子水和无水乙醇在超声清洗机中各清洗 3 min，吹干后拍摄电极表面的形貌图。溶液均用分析纯试剂和去离子水配制， 分别采用盐酸和氢氧化钠调整溶液的pH，电化学实验采用 CHI 604B 电化学工作站(上海辰华仪器公司)，实验均在室温下进行。
3 实验结果和讨论3.1扫描速度对镁铝合金在中性NaCl 阳极溶解的影响图 1 为扫描速率对在镁铝合金在 0.5 M NaCl 溶液中的线性扫描曲线。如图1b-1c 所示，电流均随着电位的增加而增加，说明镁铝合金在中性 NaCl 中的阳极溶解属于电子转移步骤控制。 由于充电和放电电流的影响， 在较高扫速(图1c)，电流达到最大；而在低扫速下(图 1a)，当电位增加到 - 0.5 V vs SCE 后出现了一个电流平台，说明此时受传质过程控制。在溶解过程中，没有出现电流峰，说明镁铝合金表面的氧化膜完全被破坏，不能抵御氯离子的侵蚀。 pH对镁铝合金在氯化钠溶液中阳极溶解过程的影响:http://www.youerw.com/huaxue/lunwen_54779.html