摘要：软质聚氨酯泡沫塑料因为拥有优异的舒适性能，在家居用品、汽车、鞋材、医疗器械等领域都得到了广泛的运用。本文将改性大豆油应用于软质聚氨酯泡沫中，以提高其性能。实验通过分别改变NCO／OH比值和改性大豆油的加入量对聚氨酯泡沫塑料进行力学性能测试，发现随着NCO／OH比值的增大，泡沫塑料的拉伸强度、撕裂强度、断裂伸长率都随之增大，但尺寸稳定性相应变差。随着改性大豆油含量的增加，泡沫塑料的拉伸强度、撕裂强度和断裂伸长率都相应减小，同时制品的尺寸稳定性随之降低。53394
毕业论文关键字：聚氨酯，大豆油，性能
Abstract： because of the excellent performance of Soft polyurethane foam, it had been widely applied to household goods, cars, shoes materials, medical equipment and other fields. In this paper, we will be modified soybean oil used in soft polyurethane foam, in order to improve its performance. Experiments tested the mechanics performance of polyurethane foam plastic by respectively changing NCO/OH ratio and the addition of modified soybean oil amount.Found that with the increase of NCO/OH ratio, Foam plastic tensile strength, tear strength, elongation at break are getting higher, but the corresponding variation dimension stability. With the increase of content of modified soybean oil, Foam plastic tensile strength, tear strength and elongation at break are reduced accordingly, meanwhile the size stability of the products decreases.
Keywords：Polyurethane, Soybean oil, performance
目录
1 绪论 4
1.1引言 4
1.2聚氨酯泡沫塑料 4
1.2.1聚氨酯泡沫塑料的基本反应 4
1.2.2聚氨酯泡沫塑料的制备工艺 5
1.3大豆油在聚氨酯泡沫塑料中的应用概况 6
1.3.1大豆油的基本概况 6
1.3.2大豆油多元醇在聚氨酯泡沫塑料中的应用概况 7
1.4本文的研究内容和意义 8
1.4.1立题的背景和意义 8
1.4.2本文研究的内容 9
2 实验部分 9
2.1 材料 9
2.1.1原料与试剂 9
2.1.2主要仪器 9
2.2 实验方法 10
2.2.1改性大豆油新型环保聚氨酯泡沫的制备 10
2.2.2力学性能测试 10
3 结果与分析 10
3.1工艺条件的考察 10
3.1.1 NCO／OH比值的影响 11
3.1.2改性大豆油含量的影响 11
3.1.3改性大豆油含量在聚氨酯泡沫体最大填充量 12
3.2聚氨酯泡沫塑料的红外光谱分析 12
结论 13
参考文献 14
致 谢 15
1 绪论
1.1引言
聚氨酯泡沫塑料在当今社会有着十分广泛的应用范围，在经济社会的方方面面都有它的身影，特别在家具、运输、冷藏、建筑、绝热等部门都有着非常普遍的应用，是人们生活中不可缺少的一种材料。同时聚氨酯泡沫塑料也是塑料中应用范围最广的一种。其中聚氨酯软泡主要应用于家具、床具及其他家用品，如沙发和枕头、靠背垫和床垫等。 大豆油在软质聚氨酯泡沫塑料中应用及性能研究:http://www.youerw.com/huaxue/lunwen_57492.html