摘要：以氧化的多壁碳纳米管-石墨烯修饰玻碳电极获得的电化学传感器，研究了重酒石酸去甲肾上腺素的电化学行为。结果表明，氧化的多壁碳纳米管-石墨烯对重酒石酸肾上腺素具有良好的电化学催化作用。在10-1000 mV.s-1扫速的峰值电流与扫描速率的线性关系表明，电极过程为扩散-吸附控制。55299

毕业论文关键词：多壁碳纳米管，石墨烯，酒石酸去甲肾上腺素，电化学传感器

Abstract：A sensor was successfully prepared by the oxidized multi-walled carbon nanotubes/ graphene modified glassy carbon electrode. The electrochemical behavior of norepinephrine bitartrate was investigated. The results showed that the oxidized multi-walled carbon nanotubes/graphene had good electrochemical activity for norepinephrine bitartrate. The linear relationship between the peak current and scan rate showed that the diffusion process with adsorption controls the electrochemistry process of norepinephrine bitartrate in the sacn rates of 10-1000 mV.s-1.

Keywords: Multi-walled carbon nanotubes, graphene, norepinephrine tartrate, electrochemical sensors

目   录

1前言 3

2材料与方法 3

2.1试剂 3

2.2仪器 3

2.3 修饰电极的制备 3

3 结果与讨论 4

3.1 多壁碳纳米管-石墨烯的扫描电镜图（SEM） 4

3.2 亚铁氰化钾在修饰电极上的电化学行为 5

3.3酒石酸-去甲肾上腺素在修饰电极上的电化学能行为 6

3.4 扫速对峰电流的影响 7

3.5 pH对峰电位的影响 8

3.6 浓度与峰电位关系 9

结论 12

参考文献 13

致谢 14

1前言

多壁碳纳米管具有较高的表面能、表面原子活性高良好的电子传递作用，在电催化和电分析化学领域中具有广阔的应用前景[1]。石墨烯作为碳纳米材料，具有促进电子转移的优点，它已经被应用于电极的修饰材料来增加电极的有效面积并增强电极表面的电子转移速率[2,3]，石墨烯复合材料具有很好的电催化活性[4]。

酒石酸去甲肾上腺素临床上主要利用它的升压作用，静滴用于各种休克，以提高血压保证对重要器官的血液供应，但使用时间不宜过长，否则可引起血管持续强烈收缩，使组织缺氧情况加重[5]。

 本文利用多壁碳纳米管经氧化获得多壁碳纳米管-石墨烯复合材料，研究了重酒石酸去甲肾上腺素在修饰电极上的电化学行为。实验表明，该方法具有较高的选择性和灵敏度，拓宽了多壁碳纳米管-石墨烯修饰电极中的应用范围。源.自|优尔,:论`文'网www.youerw.com

2材料与方法

2.1试剂

酒石酸-去甲肾上腺素，K4Fe(CN)6，,多壁碳纳米管购自深圳纳米港有限公司；所有试剂均为分析纯试剂，0.1M磷酸盐缓冲溶液（PBS）由0.1M Na2HPO4组成需PH用6M HCl及1M NaOH调节。

2.2仪器

   CHI 1230电化学工作站（美国），三电板系统；修饰电极为工作电极，铂电极为对电极，饱和甘汞电极（SCE）为参比电极，QUANTA FEG 450扫描电镜（美国）。

2.3 修饰电极的制备

多壁碳纳米管-石墨烯采用Hummers方法制备[6]：取1.00g多壁碳纳米管-石墨烯， 0.50gNaNO3, 加入70.00ml浓硫酸，冰浴，加入3.000g KMnO4，反应24h，用水稀释，加入双氧水，超声波超声2h，用稀盐酸反复洗涤，再用水洗涤，37℃真空干燥。 去甲肾上腺素在多壁碳纳米管-石墨烯修饰玻碳电极上的电化学行为:http://www.youerw.com/huaxue/lunwen_59588.html