炭黑-白炭黑双相粒子填充天然橡胶体系配方研究

时间:2021-02-27 16:50来源:毕业论文
炭黑—白炭黑双相填充剂是优良的橡胶补强剂.本文采用均匀设计法研究了CSDPF/CB/NR体系。利用线性回归得到了天然橡胶硫化胶的物理机械性能(拉伸性能、断裂伸长率、撕裂强度及耐磨

摘要炭黑—白炭黑双相填充剂是优良的橡胶补强剂.本文采用均匀设计法研究了CSDPF/CB/NR体系。利用线性回归得到了天然橡胶硫化胶的物理机械性能(拉伸性能、断裂伸长率、撕裂强度及耐磨耗性能)与配方组分的关系,得到最优配方为:CSDPF,10;Si-69,0.5;促进剂NS,1.2;防老剂,1.4;硫磺,2.4;古马隆,5;碳黑,50。在此配方下硫化胶的性能:拉伸强度26.53MPa、断裂伸长率432%、撕裂强度100 KN.m-1、磨耗体积0.3 cm3  63619

毕业论文关键词  均匀设计 CSDPF 力学性能 回归分析 

 毕业设计说明书(论文)外文摘要

Title   The study of  CSDPF filled in natural rubber    formulation 

Abstract

In this thesis, natural rubber was filled with carbon black as well as CSDPF, of which the formulation was optimized via homogeneous design. Also, the mechanical property, such as the tensile strength, tearing strength, hardness, elongation at break of the vulcanizate were measured in order to get the optimal formula, which is,CSDPF, 10; Si-69, 0.5; accelerator NS, 1.2; antioxidant, 1.4; sulfur, 2.4; coumarone, 5; carbon black, 50. In this formulation the vulcanizate properties: tensile strength 26.53MPa,  elongation at break,432% tear strength 100 KN.m-1, wear volume 0.3 cm3.

Keywords: uniform design, CSDPF, mechanical properties, regression  analysis

目  录

1. 绪论 1

1.1 引言 1

1.2  CSDPF(炭黑—白炭黑双相) 1

1.2.1炭黑 1

(1)简介 1

(2)炭黑的补强机理 1

1.2.2 白炭黑 2

(1)成分及其物理性质 2

(2)白炭黑的制备方法 2

1.2.3 CSDPF简介 2

1.2.4 CDPDF在橡胶中的研究进展 3

1.3 实验方法 — 均匀设计法 4

1.3.1 概念 4

1.3.2 结果统计分析方法 4

1.3.3 均匀设计在橡胶研究中的进展 5

1.4  本课题的目的、意义及主要研究内容 5

2  实验部分 5

2.1 实验设计 5

2.1.1 均匀设计表的选择 5

2.1.2 回归方程的选取 7

2.1.3 最优回归方程的建立 7

2.2 原材料及混炼胶配方 8

2.3 实验器材 9

2.4 CSDPF/N330/NR硫化胶的制备 9

2.5  CSDPF/N330/NR硫化胶的性能测试 9

2.5.1 硫化性能测试 9

2.5.2 拉伸性能测试 9

2.5.3 撕裂性能测试 9

2.5.4 硫化胶密度的测量 10

2.5.5 硫化胶硬度测试 10

2.5.6 硫化胶磨耗性能测试 10

2.5.6 热氧老化测试 10

3 实验结果及讨论 炭黑-白炭黑双相粒子填充天然橡胶体系配方研究:http://www.youerw.com/huaxue/lunwen_70228.html