摘 要：在Na2CO3介质中，采用电化学方法分别在玻碳电极、金电极及石墨电极表面合成了纳米金，采用纳米金修饰电极研究了重酒石酸去甲肾上腺素的电化学行为；以纳米金修饰的金电极和玻碳电极可以有效识别酒石酸及去甲肾上腺素分子。65804
毕业论文关 键 词：纳米金 电化学 重酒石酸去甲肾上腺素
Abstract：In this paper the electrochemical technology was performed for the synthesis of gold nanoparticles on the surface of gold electrode, glassy carbon electrode and graphite electrode using Na2CO3 as a stable reagent, respectively. The snowflake-like gold nanoparticles on the surface of bare electrode were obtained. Electrochemical behavior of noradrenaline-bitartrate at gold nanoparticle modified electrode was investigated. It was demonstrated that the modification of gold electrode with gold nanoparticles was a simple and effective method for the recognition of noradrenaline.
Keywords：gold nanoparticles, electricalchemistry, noradrenaline-bitartrate
目 录
1 前言 3
2 实验部分 3
2.1 试剂 3
2.2 仪器 3
2.3修饰电极的制备 3
3 结果与讨论 4
3.1 HAuCl4的循环伏安图（CV） 4
3.2 纳米Au在电极上的沉积曲线 4
3.3 GNPs的扫描电镜图（SEM） 5
3.4 纳米金修饰电极的CV曲线...............................8
3.5 亚铁氰化钾的在修饰电极上的CV曲线 9
3.6 重酒石酸去甲肾上腺素在纳米金修饰电极上的CV曲线 10
结论 13
参考文献 14
致 谢 16
1 前言
贵金属纳米材料吸引了许多研究者的关注，如在催化反应、电化学传感器、生物标记或光子材料学等方面的应用。提高电化学传感器的灵敏度是在分析化学研究领域具有非常重要的有意义。纳米金由于其显著的高催化活性和特殊的电子效应已被广泛应用于传感器领域【1-3】。纳米金的形状、组成和尺寸大小对传感器的灵敏度和分辨率有显著影响。球形纳米金粒子、金纳米线、金纳米棒和纳米星合成的已有报道,硫醇、胺、腈、羧酸、膦【4-7】等它们在纳米金的化学合成中通常作为稳定剂。然而，稳定的试剂常对传感器带来污染，并影响传感器的灵敏度和分辨率。
电化学合成是控制不同尺寸、数量、粒子间的距离和形状金属纳米颗粒的有效方法，不仅可以采用稳定剂控制，还可以通过沉积时间和不同的电极来控制该合成。论文 网
本文为了得到高灵敏度和高分辨率的传感器，用碳酸钠作为稳定剂，采用电化学技术分别在金电极、玻碳电极和石墨电极的表面合成纳米金，并对重酒石酸去甲肾上腺素在修饰电极上的电化学行为进行了研究。
2 实验部分
2.1 试剂
4mg/ml HAuCl4•4H2O，3.00g/L Na2CO3，2.50 M H2SO4, 2.00 mg/ml重酒石酸去甲肾上腺素（C8H11NO3.C4H6O6.H2O），去离子水。所用试剂均为分析纯。0.10 M NaH2PO4-0.10M KCl缓冲溶液（PBS），用1.0 M NaOH 或HCl调节pH为 7.00. 不同电极制备的纳米金对去甲肾上腺素的电化学催化:http://www.youerw.com/huaxue/lunwen_73520.html