摘要本实验将4种不同长径比的含能颗粒放置于烧杯中，然后加入配制好的丙烯酰胺灌注液，使含能材料凝聚。由于含能材料的存在，会对丙烯酰胺在其中的聚合造成影响。本文主要探究了聚合时温度、单体的浓度、引发剂的浓度、颗粒的大小以及溶剂属性等条件的影响。在烧杯中插入热电偶传感器，记录下不同时刻的温度，通过温度与时间的关系来比较反应程度，然后用将反应置于红外检测仪下，追踪其聚合过程。从而得出丙烯酰胺在细孔中聚合的边界条件。73535
毕业论文关键词 丙烯酰胺 细孔聚合 空间阻碍 红外分析
毕业设计说明书外文摘要
Title The performance research of acrylamide polymerization in pore space
Abstract In this experiment, we put four kinds of energetic particles of different of aspect ratio into the beaker。 Than the configured solution which contains AM is added up, which will cohere the energetic particles。 Because of the existence of energetic particles, polymerization of AM will be impact。 This paper mainly studied the impact to polymerization of temperature, the concentration of monomer and initiator, particle size and the selection of solvent。 The thermocouple was inserted into the beaker，which is used to record the temperature in different time。 Then the relationship between temperature and time was used to compare the degree of polymerization。 And then use IR to trace its polymerization process。 Than the boundary condition of acrylamide polymerization in pore space can be known。
Keywords acrylamide polymerization in pore space steric hindrance infrared spectrum analysis
目 次
1 引言 1
1。1 聚丙烯酰胺的性质 1
1。2 聚合方法 2
1。3 应用 2
1。4 研究背景 3
1。5 研究现状与不足 3
1。6 实验思路 4
2 实验部分 5
2。1 主要原料及仪器 5
2。2 实验配方 5
2。3 实验流程 5
2。4 测试分析 6
3 结果与讨论 7
3。1 时温分析 7
3。1。1温度对聚合反应的影响 7
3。1。2颗粒大小对聚合的影响 10
3。1。3 单体浓度和引发剂浓度对聚合反应的影响 13
3。1。4 探究丙烯酰胺空隙聚合的临界条件 14
3。2 红外光谱分析 16
3。3误差分析 19
结 论 19
致 谢 21
1 引言
1。1 聚丙烯酰胺的性质
聚丙烯酰胺的单体为丙烯酰胺（AM），其化学式为CH2=CHCONH2。丙烯酰胺是一种带不饱和键（碳碳双键）的酰胺类物质，在常温下为白色无味片状结晶。由于酰胺基团的存在，丙烯酰胺易溶于水、醚、乙醇、及三氯甲烷等极性溶剂中。在常温下会分解为二甲基胺，或是受热分解为一氧化碳、二氧化碳、氮氧化物。丙烯酰胺因为带有不饱和键（碳碳双键），在空气中或紫外线作用下会发生聚合反应。因此在储存时要注意隔绝空气，避免阳光直射。论文网 丙烯酰胺在细孔中聚合性能研究:http://www.youerw.com/huaxue/lunwen_83919.html