摘要以Fe3O4、苯乙烯、二乙烯苯和偶氮二异丁氰为起始反应物，用乳液法制得Fe3O4/PS二聚物，随后用正硅酸四乙酯、氨水采用溶胶凝胶法制得Fe3O4/PS/SiO2三聚物，用三氯甲基硅烷对其进行表面疏水改性，制得Fe3O4/PS/SiO2 纳米复合材料。用XRD、TEM、EDS等对其进行表征测定，结果表明，制得的纳米复合材料具有核壳结构、粒径均匀、分散性好，且具有磁性，是超疏水性、亲油性材料。在应用性能测试环节,对复合材料的吸油性能和循环性能进行测定，结果表明，纳米复合材料具有良好的吸油性能，对于不同种类的油类物质最大吸油量不同，吸油时间不同；同时该纳米复合材料具有良好的循环性能，对于处理溢油事故具有十分重要的意义。77142

毕业论文关键词  纳米复合材料  乳液法  溶胶凝胶法  循环性能

毕业设计说明书外文摘要

Title    Preparation and Performance Study of Environmentally    Friendly Oil Absorption Nanocomposites                         

Abstract In this paper, Fe3O4/PS dipolymers are successfully prepared by emulsion method, with Fe3O4, styrene, pinylbenzene, AIBN as reactant。 Fe3O4/PS/SiO2 terpolymers are successfully prepared by sol-gel method, with TEOS and ammonia as reactant。

Fe3O4/PS/SiO2 nanocomposites are successfully prepared by changing hydrophobicity, with methyl silicochloroform。 The nanocomposites have been well characterized by XRD、TEM、EDS method。 The results showed that the nanocomposites have core-shell structure, uniform grading, finely disseminated。 Also the nanocomposites are materials which have magnetism, super-hydrophobicity and hydrophobicity。 In the application test, nanocomposites’ absorption performance and cycle performance are measured。 The results showed that nanocomposites have  satisfactory absorption performance, for different kinds of oil, the maximum absorption and adsorption time are different。 Also nanocomposites have satisfactory cycle performance, this is very important to handle the oil spill accident。 

Keywords  Nanocomposite  Emulsion method  Sol-gel method  Cycle performance

目   次

1  引言 1

1。1  石油入海后的复杂变化 1

1。1。1  扩散 1

1。1。2  蒸发 1

1。1。3  氧化 2

1。1。4  溶解 2

1。1。5  乳化 2

1。1。6  沉积 2

1。1。7  海洋生物的降解和吸收 2

1。2  海洋石油污染的危害 2

1。2。1  生态危害 3

1。2。2  社会危害 4

1。3  海洋石油污染的处理办法 5

1。3。1  物理处理法 5

1。3。2  化学处理法 5

1。3。3  生物处理法 6

1。4  吸油性材料 7

1。4。1  传统吸油性材料 7

1。4。2  高吸油性树脂 7

1。5  本课题的主要研究内容及实验方案 环境友好型纳米吸油材料的制备及性能研究:http://www.youerw.com/huaxue/lunwen_88624.html