摘要本文通过两种方法制备钙钛矿型钛酸锶光催化剂，并使用这两种方法所制备的样品对亚甲基蓝进行催化降解实验，以此来获得所制备催化剂的催化活性，同时通过XRD及红外光谱测定来获得各自制备的样品的物质结构以及物质组成。结果表明：两种方法制备的钛酸锶催化活性、物质结构以及物质组成没有太大差别。同时本文也对各制备方法的最佳制备条件进行了探索，结果是：参与反应的各物质的加入量对产物的成胶时间、产物的相对结晶度以及产物对亚甲基蓝的催化活性均有影响。79532

毕业论文关键词：钙钛矿；钛酸锶；物质结构；亚甲基蓝

毕业设计说明书外文摘要

Title    Preparation of Sr-Ti-O solid catalyst 

Abstract In this paper, the two methods are compared for the preparation of perovskite type strontium titanate。 The activity of the prepared samples was obtained by catalytic degradation of methylene blue according to the samples prepared。 At the same time, the material structure and composition of the prepared samples were detected by XRD and infrared spectroscopy。 Results shows that two methods of preparation of strontium titanate catalytic activity, material structure and composition of the material are not much different。 We also explored the best preparation conditions of each preparation method, as a result, the amount of each substance involved in the reaction was the time to the product。 The relative crystallinity of the product and the product had an effect on the catalytic activity of methylene blue。

Keywords   Perovskite; strontium titanate; material structure; methylene blue

1绪论 1

1。1光催化剂的研究背景 1

1。2钛酸锶光催化剂的研究现状 2

1。3钛酸锶光催化剂的制备现状 2

2仪器及试剂 5

2。1仪器 5

2。2试剂 5

2。3主要分析仪器 5

2。3。1 X射线衍射仪（XRD） 5

2。3。2傅里叶红外光谱仪（FT—IR) 6

3 实验部分 7

3。1 SrTiO3光催化剂的制备实验一 7

3。1。1 采用溶胶—凝胶法制备SrTiO3的几个影响因素 7

3。2  SrTiO3光催化剂的制备实验二 7

3。2。1酒石酸的影响 8

3。2。2 去离子水用量的影响 9

3。3  SrTiO3催化活性实验 9

3。3。1亚甲基蓝标准曲线的测定 9

3。3。2  测定SrTiO3催化活性 11

4 实验结果 12

4。1 实验一制备SrTiO3的各影响因素、催化活性及其表征 12

4。1。1冰醋酸 12

4。1。2水 12

4。1。3 无水乙醇 13

4。1。4 甘油 14

4。1。5  pH值 15

4。1。6 温度 15

4。1。7  实验一最佳方法的催化活性测定 Sr-Ti-O固体催化剂的制备:http://www.youerw.com/huaxue/lunwen_92024.html