摘要：为了探究形貌均一、尺寸均匀的微纳米级结构的草酸铈的性能。利用超声化学法，以硝酸铈和草酸为起始原料，在表面活性剂聚乙烯吡咯烷酮（PVP）的帮助下，合成配位聚合物草酸铈纳米多级结构。对产物进行傅里叶红外光谱（FI-IR）、比表面积检测法（BET）、X-射线衍射分析（XRD）、扫描电子显微镜（SEM）及热重分析（TGA）表征。对实验参数，如反应时间、PVP的用量对草酸铈的形貌和大小的影响进行了分析讨论。以草酸铈为前驱体，在空气氛中煅烧得到CeO2。79625
毕业论文关键词：超声化学法，草酸铈，二氧化铈，配位聚合物，多级结构
Abstract: In order to explore the morphology, uniform size of micro/nano level structure of oxalic acid cerium performance。 Using ultrasonic chemical method to cerium nitrate and oxalic acid as starting material, the surface agent polyvinylprrolidone(PVP), with the help of synthetic coordination polymer oxalic acid cerium nano multistage structure。 Coordination polymer oxalic acid cerium has been characterized by Fu Liye infrared spectroscopy (FT-IR), specific surface area test (BET), powder X- ray diffraction (XRD), scanning electron microscopy (SEM) and thermal analysis (TGA)。The experimental parameters, such as reaction time, the amount of PVP’s influence on the morphology and size of oxalic acid cerium is analyzed and discussed。By using the cerous oxlate as precursor, CeO2 has been obtained through calcination in atmospheer。
Keywords: ultrasonic chemical method, cerous oxlate, cerium oxide, coordination polymer, hierarchical structure
目录
1 前言 3
2 实验部分 3
2。2 试剂 3
2。3 对苯二甲酸铈的制备 4
2。4二氧化铈的制备 4
3 结果与讨论 4
3。1 草酸铈的XRD分析 4
3。2草酸铈的FT-IR分析 5
3。3草酸铈的TGA分析 6
3。4草酸铈的UV的分析 6
3。5草酸铈的荧光分析 7
3。6草酸铈的SEM分析 8
3。6。1反应时间对草酸铈结构的影响及形成机理 8
3。6。2表面活性剂PVP量对草酸铈结构的影响 10
3。7煅烧类长方形草酸铈制得样品的分析 11
3。7。1二氧化铈的SEM分析 11
3。7。2二氧化铈的BET分析 12
3。7。3二氧化铈的XRD分析 13
结 论 15
参考文献 16
致谢 17
1 前言
纳米材料（NsM）的概念最初是在80年代初期由德国学者Gleiter教授提出并首次获得人工制备的纳米晶体[1]。纳米材料又称超微细材料，是由微小颗粒——绝大多数是晶体，其特征尺度至少在一个方向上为纳米量级——组成的固体，其典型的晶粒尺度为1-100nm[2]。随着纳米材料的出现，世界各国开始广泛关注，并逐渐开展了对这种新材料的研究工作。
金属有机配位聚合物具有结构的多样性以及广阔的应用前景，备受化学家、物理家、材料学家的关注。金属中心的导电、荧光、氧化还原和催化特性以及高分子材料优良的溶解性能、柔性以及成型性能而备受关注[3]。当金属有机配合物颗粒尺寸达到纳米级别时，即使不改变化学组成，也可能产生新的物理化学性能[4]。论文网 类长方形微纳米草酸铈的可控合成:http://www.youerw.com/huaxue/lunwen_92185.html