摘要：硅酸盐黏土矿石―凹凸棒土具有比表面积大、化学稳定性好、吸附能力强等特点，其可作为良好的吸附材料。本文基于凹凸棒土此优良吸附特性，采用水热合成的方法并用正丙胺对其改性来研究制备改性凹土吸附剂。首先，用3 mol/l的盐酸浸泡精致凹凸棒土3 h，再用质量分数为3%的氯化铵与凹凸棒土混合，于箱式电阻炉中500℃焙烧3小时，自然冷却后取出再添加质量分数为6%的正丙胺进行水热合成改性。此外，对改性后的凹土吸附剂进行了形貌分析和BET分析，凹土吸附剂的比表面积由145。6 m2/g增加到164。8 m2/g，得到明显增加。81897

毕业论文关键字：凹凸棒石黏土，正丙胺，水热合成，吸附剂

Abstract:Silicate clay minerals-attapulgite has large surface area,good chemical stability,strong adsorption capacity and other characteristics,which may serve as a good adsorbent material。Based on this excellent adsorption characteristics of attapulgite and modified with n-propylamine to study its preparation pronting adsorbent by hydrothermal synthesis method。First,with 3 mol/l hydrochloric acid soak refined attapulgite 3 h,and then the mass fraction of 3 ammonium chloride soil mixed with attapulgite, box-type resistance furnace at 500℃ calcined for 3 hours, allowed to cool and then remove the add the mass fraction of 6% n-propylamine hydrothermal synthesis modification。 In addition, modified attapulgite adsorbent were analyzed morphology analysis and BET specific surface area of attapulgite adsorbent by 145。6 m2/g to 164。8 m2/g, significantly increased。

Keywords：attapulgite clay，n-propylamine，hydrothermal synthesis，adsorbent

目录

1前言 3

1。1凹凸棒石黏土简介 3

1。3凹凸棒土的资源利用现状 7

1。4课题意义 10

2吸附剂的制备 10

2。1吸附剂的特性及其分类 10

2。2凹土吸附剂合成机理 11

2。2水热合成 12

2。3吸附剂的制备 13

2。3。1凹凸棒土的预处理 13

2。3。3凹凸棒土的改性 15

2。3。4吸附剂的制备 15

3吸附剂的表征 15

3。1吸附剂的形貌及组分分析 15

3。2吸附剂的BET分析 16

结论 19

参考文献 20

致谢 22

1 前言

随着国民经济的快速发展，石油类加工产品已广泛地应用于国民经济的各个领域和人类的日常生活，需求量与日俱增，但同时也带来对大气、水体的污染。随着人民的生活水平不断提高，世界各国对环保也愈发重视。目前含油废水的处理和空气的净化已成为环境治理和保护的一项重要内容[1]。

凹凸棒土具有较大的比表面积与离子交换容量、良好的吸附脱能力、热稳定性，而且价格低廉，在污水、废气的处理中具有很大的应用潜力。但同时凹凸棒土表面有很多羟基，表面具有亲水疏油性，极易形成聚集体，分散性能差，难以分散在其它介质中，因此需对凹凸棒土进行表面改性处理。

1。1凹凸棒石黏土简介