摘要：本文对水性膨胀型防火涂料（AIFRC）的阻燃体系及填料组分的种类和用量进行了研究，并通过大量实验完成了水性膨胀型防火涂料配方的优化。涂料以聚磷酸铵（APP）-季戊四醇（PER）-三聚氰胺（MEL）为阻燃体系、水性丙烯酸乳液为粘结剂、各种不同的无机粉体为填料，并添加适量的水。通过TG-DTA和FT-IR对水性膨胀型防火涂料的表征结果发现，不同的阻燃体系比例或者不同的无机填料及用量对涂料受热分解碳化的过程有较大的影响，从而影响了涂料的防火阻燃性能。最后，在实验中得出：单组份填料，氢氧化铝阻燃效果最好，加入的量和阻燃效果成正比；双组份填料，二氧化钛和氢氧化铝的量为1:1时，阻燃效果最好；三组份填料，二氧化钛、氢氧化铝和硼酸锌的量为1:1时，阻燃效果最好。82105
毕业论文关键词：水性膨胀型防火涂料 阻燃体系 无机填料 阻燃机理
The study effect of inorganic packing on expansive fire retardant coating
Abstract: In this paper, the type and dosages of fillers and the flame-retardant system of waterborne intumescent fire-retardant coatings have been studied, and the optimum formula of waterborne intumescent fire-retardant coating has been decided by a lot of experiments。 Using ammonium Polyphosphate (APP)-Pentaerythritol (PER)-Melamine (MEL) as fire-retardant system, various inorganic powders as the fillers, acrylic emulsion as binder。 Besides, appropriate water was added。 The TG-DTA and FT-IR were used to characterize the waterborne intumescent fire-retardant coatings, and the results reveal that different fire-retardant system or different inorganic fillers have great effects on the procedure of decomposition and carbonization of the coating, which affects the fire-retardant properties of the coating。
Key words：Waterborne intumescent fire-retardant coatings; Fire-retardant system; Inorganic filler; Flame-retardant mechanism
目 录
1 绪论 1
1。1 防火涂料的分类 1
1。2 膨胀型防火涂料 1
1。2。1 膨胀型防火涂料的组分及作用 2
1。2。2 膨胀型防火涂料的阻燃机理 2
1。3无机填料对涂料阻燃效果的影响 3
1。3。1 二氧化钛 3
1。3。2 硼酸锌 3
1。3。3 氢氧化铝 3
1。3。4 硅藻土 4
1。3。5 玻璃纤维 4
1。4 本文研究的内容及意义 4
1。4。1 研究内容 4
1。4。2 研究意义 4
2 实验部分 5
2。1 实验试剂 5
2。2 实验仪器 5
2。3 水性膨胀型防火阻燃涂料（AIFRC）的配制 5
2。4 试板的制作 6
2。5 防火性能测试方法 6
2。5。1 测试方法依据标准 6
2。5。2 小室燃烧法 6
2。7 填料及涂料的测试与表征 7
2。7。1 填料的粒径大小测试方法及结果 7
2。7。2 傅立叶红外（FT-IR）表征 无机填料对膨胀型防火涂料的影响研究:http://www.youerw.com/huaxue/lunwen_96229.html