摘  要：本论文主要介绍了聚甲基丙烯酸水凝胶的制备、特性表征等方面的知识。聚甲基丙烯酸水凝胶是以MAA单体为原料，过硫酸钾为引发剂，N,N-亚甲基双丙烯酰胺为交联剂而制备成的；大体上研究了聚甲基丙烯酸水凝胶在蒸馏水中、交联剂和引发剂不同用量、不同pH、不同食盐水浓度下的溶胀率。经实验发现：在不同温度，不同配比的情况下，溶胀率不是一成不变的；经过一定的实验研究，制备凝胶温度定在60 °C，N，N-亚甲基双丙烯酰胺用量是单体量的1 %、过硫酸钾用量是单体量的3 ％时，得到的凝胶较好。溶胀性能在pH=8时是最佳的。聚甲基丙烯酸水凝胶具备明显的pH酸碱敏感性，随着一系列浸泡溶液pH值的变大，体系的溶胀度也随着变大。82134

毕业论文关键词：甲基丙烯酸水凝胶；溶胀率；溶胀性能

Preparation of Poly - Methyl Acrylic Acid Hydrogel

Abstract: In this paper, we mainly introduce the preparation and characterization of poly - methyl acrylic acid hydrogel。 Poly (methyl methacrylate) hydrogel consists of a MAA monomer used as raw materials and potassium persulfate as initiator, N, N-methylene bisacrylamide as crosslinking agent;  In general，we studied the swelling rate of poly (methyl methacrylate) hydrogel in distilled water, crosslinking agent and initiating agent of different dosage, different pH, and the different saline concentration。The experiment results show that the swelling ratio is not static at different temperatures。After that certain experimental research, we set the gel temperature at 60 °C, N, n-methylenebisacrylamide dosage is monomer 1 %, potassium persulfate dosage is 3 % of the monomer,  the swelling ratio is better。 Swelling properties are optimal when pH is 8。 The poly methyl acrylic acid hydrogel had obvious pH sensitivity, and the temperature sensitivity。

Key words: Methyl acrylic hydrogels;  Swelling rate; Swelling performance

目    录

摘 要 1

引 言 2

1实验部分 2

1。1 仪器与试剂 2

1。2 制取聚甲基丙烯酸水凝胶的过程 2

1。3 计算出凝胶的溶胀率 2

2结果与讨论 3

    2。1聚甲基丙烯酸水凝胶溶胀性能的测定 3

2。2交联剂的多少影响水凝胶的溶胀比 4

2。3引发剂的用量影响水凝胶溶胀比 4

2。4聚甲基丙烯酸水凝胶对酸碱性（pH）敏感性的研究 5

2。5离子浓度对水凝胶溶胀比的影响 6

3总结 7

参考文献 8

致谢 9

聚甲基丙烯酸水凝胶的制备引 言

    水凝胶是以水为分散介质的一种凝胶；是在具有交联结构的水溶性高分子中引入一部分疏水基团而形成的能够遇到水就能膨胀的交联聚合物；为高分子网络体系，性质比较柔软，通常能保持一定的形状，可以大量的吸水。只要是水溶性或亲水性的高分子，他们通过一定的化学交联或物理交联，都可以形成水凝胶。水凝胶表现在对pH、温度、光、溶剂组成、离子强度、压力电场等外界环境反应敏感 ，在药物控释、记忆原件开关、化工分离、生物工程等领域具有良好的应用。文献综述