ZnGa2O4光催化材料的制备及其降解酸性红1染料的研究

摘要：本文以Ga2O3为牺牲模板剂，采用水热法和固相法合成ZnGa2O4光催化材料。ZnGa2O4为尖晶石结构，是具有d10结构的半导体材料，它在材料，光催化领域都得到广泛应用，并且具有良好的发展前景。在降解酸性红1染料溶液的过程中，该样品表现出了良好的光催化活性。将样品用紫外可见分光光度计、X射线粉末衍射仪、透射电子显微镜等进行表征，表明所制备的ZnGa2O4样品光催化活性较好，且对酸性红1染料溶液去除率最高可达100 %。83471

毕业论文关键词：ZnGa2O4光催化剂；光催化；酸性红1染料

Study on Preparation and Photocatalytic Degradation of Acid Red 1 dye of ZnGa2O4

Abstract: In this paper, we use Ga2O3 as a sacrificial template to synthesis ZnGa2O4 photocatalytic material by hydrothermal synthesis and solid phase method。 ZnGa2O4 has spinel structure and it is a semiconductor material with a d10 configuration。 It has good prospects for development, which has been widely used in the material and photocatalytic area。 In the process of degradation of acid red 1dye solution, the sample showed a good photocatalytic activity。 UV-visible spectrophotometer, X-ray diffraction and transmission electron microscope showed that the photocatalytic activity of ZnGa2O4 photocatalyst was good and the removal rate of acid red 1 dye solution can be reached 100 %。

Key Words: ZnGa2O4 photocatalyst; Photocatalytic; Acid red 1 dye

摘要 1

引言 1

1 实验部分 3

1。1 实验仪器及试剂 3

1。2 实验方法 3

1。3 表征分析 4

1。4 光催化实验 4

2 结果与讨论 4

2。1 物相分析 4

2。2 形貌分析 5

2。3 紫外-可见漫反射分析 5

2。4 ZnGa2O4样品的光催化评价 6

2。5 ZnGa2O4降解酸性红1染料溶液的机理分析 7

3 结论 7

参考文献 8

致谢 10

ZnGa2O4光催化材料的制备及其降解酸性红1染料的研究

引言

进入二十一世纪以来，随着工业化程度的不断提高，工业化水平以前所未有的速度迅猛发展，给我们的生产、生活带来了极大的便利，提高了我们的生活水平。但与此同时，工业化水平的提高，不可避免的也带来一定程度的环境污染[1]以及能源问题。论文网

毫无疑问，环境污染[3]是当今社会面临的重大问题，如何有效地解决这个问题是众多研究者工作的方向。传统的光催化剂，如TiO2选择性差、稳定性低、技术不够成熟[4]，使得催化效果一般因此，找出一种新型、高效的光催化材料[5]降解水体中含有的有机组分，是现如今许多研究者关注的焦点。1972年，科学家Honda和Fujishima二人共同报道出，能够使用TiO2单晶电极，光催化分解水来制取氢气，自此，光催化技术便受到学者们的广泛关注[6]。很多学者都在光催化方面进行了深入的探讨，并为此做了大量研究，其研究方向主要涉及光催化材料的作用机理、稳定性、反应条件以及它的耗能情况。Carey等[7]人将TiO2粉体成功应用于紫外光催化分解降解水体中的有机污染物。光催化反应高效、耗能较低、副反应较少，反应在常温常压下就能进行[8]，这是光催化的优点。 ZnGa2O4光催化材料的制备及其降解酸性红1染料的研究:http://www.youerw.com/huaxue/lunwen_98415.html