摘要本文通过实验研究了激光辐照时间、激光功率对碳纤维复合材料的烧蚀影响，发现在短脉冲辐照下，辐照时间对质量烧蚀率和热烧蚀率没有太大影响，损伤程度随激光功率的增大而增大；在长脉冲辐照下，质量烧蚀率和热烧蚀率随激光功率的提高而增大；在连续激光辐照下，辐照时间在不同的激光功率时对热烧蚀率和质量烧蚀率的影响不太相同，但损伤情况与激光功率呈正相关。观察烧蚀后表面情况发现，长脉冲的烧蚀斑与短脉冲和连续激光有所不同，长脉冲的烧蚀斑小而深，短脉冲和连续激光烧蚀斑面积很大。87553

毕业论文关键词 碳纤维材料 激光烧蚀 长脉冲 连续激光

毕业设计说明书外文摘要

Title    不同脉宽激光辐照碳纤维复合材料的毁伤效果比较               

Abstract In this paper, the ablation effect of laser irradiation time and laser ablation power on the carbon fiber composite material is learned, founding that in short pulse irradiation, irradiation time has little impact on the thermal ablation rate and mass ablative rate, with the increasing degree of damage laser power increases; Under the long pulse irradiation, thermal mass ablation rate and mass ablation rate increase with increasing laser power; Under continuous laser irradiation, the effect on thermal ablation rate and mass ablation rate at different laser power caused by irradiation time is not the same, but the damage was positively correlated with the laser power。 Observed the surface of the material after ablation founding that the ablation spot caused by long pulse is different with short pulse and continuous laser , long-pulse ablation spot is small and deep。 Ablation spot caused by short pulsed and continuous laser are bigger。源-于,优~尔^论=文.网www.youerw.com 原文+QQ7520~18766

Keywords：Carbon fiber  long-pulse  laser ablation  continuous laser

目   次

1  引言 1

1。1 研究背景 1

1。2 研究方法 1

1。3研究意义 2

2  理论基础 2

2。1  实验原理 2

2。2  国内外成果 3

3  实验过程 5

3。1  实验材料及仪器 5

3。2  实验方法及实验光路 5

3。3  实验步骤 5

4  实验结果分析 7

4。1 辐照时间对碳纤维复合材料热烧蚀率和质量烧蚀率的影响 7

4。2 不同辐照功率对碳纤维复合材料热烧蚀率和质量烧蚀率的影响 10

4。3 长脉冲激光下不同脉宽对热烧蚀率、质量烧蚀率影响 13

4。4 实验现象的分析 14

结  论 17From+优 尔-论+文W网www.youerw.com 加QQ752018`766

致  谢 18

参 考 文 献 19

1  引言

1。1  研究背景

碳纤维复合材料具有耐高温、耐腐蚀、结构稳定以及材料性能易于设计等一系列优良属性，它质量轻承重能力强，有些情况下自身还能发挥一些特殊功能，目前能够拥有像碳纤维复合材料这么多优良特性的材料几乎没有，因此，碳纤维复合材料的出现就意味着其拥有宽广的应用前景，近些年我们也可以看到碳纤维材料正一步步成为空间发射器等产品的首选材料。 (责任编辑：qin)