摘要双碱光电阴极制造工艺简单，制作成本低廉，响应速度较快，在300-650nm的范围内灵敏度较高，因此被广泛应用于光电倍增管等光电器件中。本文首先对光电阴极进行了概述，然后对锑钾铯光电阴极的特征以及它的制备工艺进行了探索，然后提出了光电阴极量子效率测试的方法及其他特性的测试方法。最后，通过对光电发射过程的分析，讨论了从采用增透膜，优化光电阴极厚度，优化组分，优化制备工艺，多信息实时监控，减小复合速率等方面来提高双碱阴极上的量子效率。77980

毕业论文关键字双碱阴极制造工艺量子效率测试量子效率

Title Research on technology of high quantum bialkali

AbstractBialkali is widely used in optoelectronic devices,such as photoelectric multiplier tube because of its simple manufacturing process,cheap

cost ,quick speed of response and high sensitivity between 300nm to 650nm。 This essay firstly introduces the photocathode，then explores the feathures and manufacturing processes of K2CsSb Bialkali。Next,propose the method of quantum efficiency and other characteristics test of photocathode。At the end of the essay,through analysizing the process of photoelectric emission,several methods have been proposed to improve the quantum efficiency of bialkali,including adopting antireflective coatings,optimizing the thickness of photoelectric cathode , component and manufacturing process,real-time monitoring of multi information and reducing composite rate。

Keywords Bialkali manufacturing process quantum efficiency test quantum efficiency

目 次

1 绪论 1

1。1 光电阴极的发展概况 1

1。2 双碱光电阴极的发展概况 2

1。3 多碱光电阴极的发展概况 3

1。4 本文研究的意义 3

1。5 本文研究的内容 3

2 锑钾铯锑钾铯双碱光电阴极特征及其制造工艺研究 5

2。1 锑钾铯双碱光电阴极特征 5

2。2 锑碱光电阴极的制造工艺研究 5

3 光电阴极的特性测试 9

3。1 评价光电阴极特性的主要参量 9

3。2 光电阴极的光电发射过程 9

3。3 锑钾铯光电阴极的量子效率测试 10

3。4 锑钾铯光电阴极的相对光谱响应特性测试 15

3。5 锑钾铯光电阴极的绝对光谱响应特性测试 15

4 提高锑钾铯光电阴极的量子效率 17

4。1 采用增透膜 高量子双碱阴极技术研究:http://www.youerw.com/tongxin/lunwen_89740.html