摘要采用不同的焊接参数对2。8mm后的6013-T4和7003两种铝合金进行搅拌摩擦焊对接。利用金相显微镜、电子万能试验机、扫描电子显微镜等方法，研究了焊缝表面形貌、金相组织、接头拉伸性能、高倍电镜下微观组织以及交换焊接前进侧后退侧后的各项参数变化。结果表明，采用搅拌摩擦焊可获得高质量的6013-T4和7003异种铝合金对接接头；搅拌头转速在800r/min、焊速在400mm/min时可以获得好的焊缝成形，接头抗拉强度可达到308MPa；在改变前进侧与后退侧后即7003铝合金为前进侧，6013铝合金为后退侧，焊接接头抗拉强度降低，交换后接头强度为交换前的93%~95%。87016

毕业论文关键词：搅拌摩擦焊；异种铝合金；力学性能；微观组织

Abstract 6013-T4 and 7003 Al alloy with hhickness of 1。8mm was carried out by stir welding (FSW) with different parameters。 By using the metallurgical microscope,electroic universal test machine and scanning electron microscope，apperance of weld, microstructures, mechanical properties, microstructure under high power electron microscope and the change of welding parameters on the advancing side back side of the exchange were investigated。The results show that,the 6013-T4 and 7003 Al alloy can be welded by FSW。In the condition of rotation speed 800r/min and welding speed 400mm/min,good apperance of weld can be got,and the tensile strength achieves 308Mpa。In the exchange of forward side and back side ,the tensile strength of the joint is slightly reduced and achieves 93%~95% of the exchange。

Key words: FSW; dissimilar alloy; mechanical property; microstructure

目录

第一章 绪论 1

1。1异种铝合金搅拌摩擦焊研究背景及意义 1

1。1。1铝合金搅拌摩擦焊背景 1

1。1。2搅拌摩擦焊原理 1

1。1。4异种铝合金搅拌摩擦焊的国内外研究现状 6

第二章 试验材料、设备及方法 8

2。1试验材料 8

2。2试验方法与设备 8

2。2。1焊接工艺试验 8

2。2。2接头拉伸试验 9

2。2。3金相组织分析 10

2。2。4断口形貌分析 10

2。2。5物相分析试验 10

第三章 试验结果及分析 12

3。1不同焊接速度对焊缝成形的影响 12

3。1。1不同焊接速度对焊缝成形的影响 12

3。1。2 7003为前进侧，6013为后退侧对焊缝成形的影响 17

3。2不同焊接参数对焊缝拉伸强度的影响 19

3。2。1 不同焊接速度对焊缝强度的影响 19

3。2。2 改变前进后退侧对接头抗拉强度的影响 22

3。3微观组织对接头抗拉强度的影响 24

3。3。1 不同焊接速度下的微观组织金相分析 24

3。3。2 500mm/min焊接速度的焊缝微观组织性能分析 28

3。3。3 400mm/min焊接速度的焊缝微观组织性能分析 31