摘要泡沫多孔陶瓷经过数十年的研究发展应用目前有着明亮的使用前景，在整个工业应用中体系也愈趋完整。现阶段工业应用中泡沫陶瓷的普遍制备方法是用有机模板浸渍法。但考虑其制备繁琐，条件限制多：制品形状，二次挂浆等。本文采用添加造孔剂法，该法操作、原理简单，具体操作原理在下文具体说明。泡沫陶瓷制备完成后用SEM、XRD、万能力学试验机设备对陶瓷进行性能的测试及表征。该泡沫陶瓷是由少量的莫来石相和主要的氧化铝相构成的。结果表明，碳在800℃时的失重会达到最大，考虑到生成了二氧化碳，所以烧结的时候在800℃进行保温，会使基体的气体完全挥发。石墨作为造孔剂对制备泡沫陶瓷气孔率的影响是石墨所用质量分数越多，陶瓷孔隙率越大，但是基体的强度会大幅度下降。87808

毕业论文关键词  氧化铝泡沫陶瓷  添加造孔剂法  石墨 

毕业设计说明书外文摘要

Title         The Preparation Techniques and Research of Alumina Ceramic Foam                     

Abstract Ceramic foam tends to enjoy a bright and promising future after researching and developing for decades before。 And in the whole manufacturing and application part, this technology is currently much more refined。 Contemporary ceramic foam applied industrially is generally manufactured through organic-template dipping。 Considering the complicated operations and limits of products shapes and secondary pulping, in this paper, we carry out the experiments by addition of pore-forming agent, which is simplified to operate theoretically。 And the details are given thoroughly in the paper below。 After preparing the ceramic foam, we apply SEM, XRD, Multi-functional force testing machine and TG to characterize and test the material。 And turns out, foam ceramic is composed of small amounts of mullite phase and main phase composition, alumina。 Consequently, TG of carbon forms reaches the peak at the temperature of 800℃, which produce CO2 in the process。 Therefore，terminating the continual heating is bound to volatilize the gas form in the carrier。 The effect of graphite as pore forming agent on the porosity of ceramic foam is the more weight fraction, the greater the porosity of the ceramic, but the strength of the matrix will decrease greatly。 

Keywords  Alumina Ceramic Foam  Foaming  Pore-forming agent  Graphite 

目   次

  1  引言 1

  1。1  氧化铝的性能及其行业前景 2

  1。2  泡沫陶瓷的应用 2

  1。3  泡沫陶瓷的研究背景及国内外如今的研究状况 5

  1。4  泡沫陶瓷的性能系数和评价指标 6 

  1。5  氧化铝泡沫陶瓷的增韧机制 7源-于,优Y尔E论W文.网wwW.yOueRw.com 原文+QQ752018`766

  1。6  泡沫陶瓷的制备工艺 8

  2  实验方法 9

2。1实验所用原料及器械  9

2。2  实验工艺流程 10

3  实验表征及结果分析12

3。1  XRD分析12

3。2  SEM分析和显微表面组织观察13

3。3  密度（气孔率）15

3。4  抗压强度16

结论 18

致谢 19

参考文献20

1  引言

    二十世纪以来，陶瓷材料愈发得到来自科学界的高度重视，而人们趋向于将20世纪中后期科学研究涌现出的陶瓷材料称为新型陶瓷，现阶段新型陶瓷材料被受业界关注。陶瓷材料在不同工况下可得到不同优异性能的应用，这一点和金属材料很相像。这两种材料在应用方面可以互相弥补优劣性，这也形成了陶瓷材料-金属材料构成复合材料的设计和发展。既增强了金属材料的延展、韧性、导电导热的能力，也同时兼具陶瓷材料的高弹性模量、硬度高、耐腐蚀磨损和导热性好等优良性能。