摘要黑磷量子点作为一种近两年才合成出来的二维晶体材料量子点，因其优异的电子学、光电学性质，继石墨烯量子点、TMDs量子点之后被人们赋予很高的期望。锑作为黑磷的同主族元素，计算表明存在类石墨烯结构的锑烯，并且具有良好的稳定性及其他优异的性能。本文采用液相剥离的方法首次成功地制备出了锑烯的量子点。采用的溶剂为NMP,超声功率为720W，超声时间为5h，离心转速为7000rpm,离心处理时间为10min。制备的锑烯量子点的横向粒径尺寸主要分布在4。6nm～6。8nm。拉曼光谱测试结果证明制备的锑烯量子点具有较好的晶体质量和稳定性。这为进一步深入开展新型锑烯量子点的研究工作奠定了基础。87822

毕业论文关键词：  二维晶体材料、  锑烯、  液相剥离法、   量子点

毕业设计说明书外文摘要

Title          The preparation of quantum dots of a new two-dimensional crystal material                             

Abstract Black phosphorus quantum dots (BPQDs), as novel two-dimensional material quantum dots which were invented in 2014, have shown excellent electric and photoelectric properties。 After graphene quantum dots and TMDs quantum dots, BPQDs have been regarded as one of the most promising materials。 Antimony and phosphorus are congeners and theoretical calculations predicted that two-dimensional anitmonene with similar structure to graphene may exist。 In this article, we successfully produced Sb quantum dots (SbQDs) using liquid exfoliation。 The solvent is NMP, the sonication power is 720W and the sonication time is 5 hours。 The dispersion was centrifuged at 7000 rpm for 10 min。 The obtained SbQDs have a lateral size of 4。6～6。8 nm。 The as-synthesized SbQDs have good stability and crystal quality proved by Raman spectroscopy。

Keywords:  two-dimensional crystal material,  antimonene,  quantum dots,  liquid exfoliation   

目   次

1  绪论 1

1。1  二维晶体材料量子点的发展 1

1。1。1  石墨烯量子点（Graphene Quantum Dots） 1

1。1。2  过渡金属硫族化合物 2

1。1。3  黑磷量子点（Black Phosphorus Quantum Dots） 3

1。2  液相剥离方法的发展 3

1。2。1  液相剥离方法的原理 4

1。2。2  液相剥离法剥离溶剂 4

1。2。3  其他制备量子点的方法 5

1。2。4  液相剥离法和其他制备量子点方法的比较 6

1。3  锑烯概念的提出 6

2  实验材料、仪器及试验方法 8

2。1  实验材料及设备 8

2。1。1  实验材料 8

2。1。2  实验设备 8源-于,优Y尔E论W文.网wwW.yOueRw.com 原文+QQ752018`766

2。2  实验方法 8

3  实验结果及分析 10

3．1  材料的表征方法 10

3。1。1  透射电子显微镜 10

3。1。2  拉曼光谱分析