摘要:本文的目的是为了研究不同热处理条件对于轴承钢零件的残余奥氏体含量的影响。运用一种便利的新方法——比容差法，来测量轴承钢零件在不同热处理条件下比容的变化，来分析残余奥氏体含量的变化。结合XRD衍射法，来测量出不同热处理条件下轴承钢零件中残余奥氏体含量。将其实验结果和比容差法进行校验，再次验证比容差法的可行性。本文通过对两种轴承钢进行相关实验，根据实验结果可以得出结论，深冷温度的降低会使残余奥氏体含量下降。87925

毕业论文关键词：轴承钢；残余奥氏体；比容差法；热处理

Measurement and Analysis of Residual Austenite Content in Bearing Steel Parts 

Abstract: The purpose of this paper is to study the effect of different heat treatment conditions on the retained austenite content of bearing steel parts。 The change of residual austenite content was analyzed by using a convenient new method - tolerance method to measure the specific volume change of bearing steel parts under different heat treatment conditions。 The content of  retained austenite in bearing steel parts under different heat treatment conditions were measured by XRD method。 The experimental results and the tolerance method are verified and the feasibility of the tolerance method is verified again。 Based on the experimental results, it can be concluded that the increase of quenching temperature will decrease the retained austenite content。

Keywords：Bearing steel; residual austenite; specific tolerance method; heat treatment

目    录

1  绪论 3

1。1  轴承钢简介 3

1。2  轴承钢分类 3

1。2。1  高碳铬轴承钢 4

1。2。2  渗碳轴承钢 4

1。2。3  高温轴承钢 4

1。2。4  不绣耐烛轴承钢 4

1。3  轴承钢的热处理工艺 4

1。3。1  预备热处理 4

1。3。2  最终热处理 5

1。4  深冷 5

1。5  残余奥氏体的测量方法 6

1。5。1  磁性测量方法 6

1。5。2  金相测量方法 6

1。5。3  X射线衍射法 7

1。6  比容差法 7源-于,优Y尔O论U文.网wwW.youeRw.com 原文+QQ75201,8766

1。7  选题的目的和意义 8

1。8  课题的研究内容 9

2。实验部分 10

2。1实验材料及热处理工艺 10

2。1。1 实验材料 10

2。1。2 热处理方式 11

2。2 比容差法实验 12

2。2。1。  实验原理 12

2。2。2 比容差法取样方法 12

2。2。3 实验仪器 12

2。2。4 实验仪器的改进 12