摘要实验合成了聚丙烯酸铵盐和聚苯乙烯-丙烯酸（苯丙）分散剂，探讨了上述两类分散剂 及与 PEO-PPO（聚氧乙烯-聚氧丙烯）表面活性剂复合后分别对三氧化二锑和十溴二苯乙烷 两阻燃剂分散性能的影响。结果表明：不论是三氧化二锑，还是十溴二苯乙烷，苯丙分散剂（单体比例 1:1）的分散性能均优于聚丙烯酸铵盐类；当其摩尔分数在 0。25～1 范围内，苯 丙和 PEO-PPO(L35 型)的复合对三氧化二锑都具有优良的分散性能；苯丙的摩尔分数在 0。25 时，与 L35 的复合分散剂对十溴二苯乙烷有最佳分散效果。在一定范围内，随着复合分散剂 用量的增加，体系的粒径在减小。88222

Abstract In this paper, acrylic acid (AA) as monomer, ammonium persulfate as initiator, water as solvent, synthetic polyacrylic acid ammonium salt dispersant and acrylic acid (AA) and styrene (St) as comonomer, isopropyl alcohol as solvent The dispersion properties of styrene - acrylic resin on antimony trioxide and decabromodiphenyl ethane - based flame retardants。 In this study, the effects of single factor and complex dispersion on the dispersibility of decabromodiphenyl ethane and antimony trioxide were studied。 The results show that It is difficult for the single dispersant to form a stable flame retardant dispersion system。 The best dispersing properties of antimony trioxide and decabromodiphenyl ethane are carried out by using styrene-acrylic dispersant and L35 complex dispersant。

毕业论文关键词：聚丙烯酸铵；苯丙分散剂； 高分子分散剂；阻燃剂； 分散稳定性

Keyword: Ammonium polyacrylate ;Styrene-acrylic；Polymer Dispersant; Flame Retardant  ；Dispersion Stability

目录

1。绪论 6

1。1 引言 6

1。2 阻燃材料源-于,优W尔Y论L文.网wwW.youeRw.com 原文+QQ75201,8766概述 5

1。2。1 高聚物阻燃机理 5

1。2。2 溴系阻燃 5

1。2。3 锑系阻燃 6

1。2。4 阻燃剂在溶液中的分散 6

2。 实验部分 6

2。1 实验设备 8

2。2 实验试剂 7

2。3 聚丙烯酸铵的制备 8

2。4 苯乙烯-丙烯酸铵分散剂的制备 9

2。4。1 实验仪器及来源 9

2。4。2 实验原料和试剂 9

2。4。3 合成方法 9

2。5 聚丙烯酸铵分散剂的表征 9

2。6。分散剂对十溴二苯乙烷和三氧化二锑的分散性能测试 10

2。6。1 分散体系分散粘度 10

2。6。2 分散体系分散稳定性 10

2。6。4 分散体系分散细度 10

2。6。5 离心法测沉降率 12

3。   实验结果讨论 11

3。1 聚丙烯酸铵分子量的变化 11

3。1。1 链转移剂对聚丙烯酸铵分子量的影响 11

3。1。2 引发剂对聚丙烯酸铵分子量的影响 12

3。2 聚丙烯酸铵对三氧化二锑和 DBDPE 的分散