摘要：汽车用胶管种类主要分有燃油胶管、空调胶管、散热器胶管、动力转向管、制动胶管、涡轮增压胶管。当然这些汽车胶管用途不同，所以对于它们各自的性能要求也是各不相同的。比如动力转向胶管接触介质是矿物油，要求耐热性能好、接头部位牢固。在我们这次研究中，主要以氯化聚乙烯橡胶（CM）为主，其他几种橡胶为辅，分别研究了增塑剂（DOP）、炭黑、促进剂（NA-22）、还有各种偶联剂的处理的碳酸钙用量等因素对橡胶硫化后的性能影响。随着DOP含量的增加，CM橡胶的硬度在不断减小。随着NA-22用量的增加，CM橡胶的拉伸强度一直都在19MPa左右；硬度在不断增加。随着炭黑用量的增加，CM橡胶的拉伸强度先上升后下降，最高达到19.52MPa；老化后橡胶的拉伸性能都有所上升，但是到达一定的老化时间后，拉伸性能有所下降；扯断变形率和永久变形率都在随着老化时间的增加而减小。钛酸酯偶联剂处理的碳酸钙对橡胶性能的影响最稳定，铝钛复合偶联剂的影响最显著。42336
毕业论文关键词：汽车胶管；氯化聚乙烯橡胶(CM)；增塑剂；促进剂；炭黑；偶联剂；
Preparation and Performance Analysis of Automotive Rubber Hose
Abstract: The main types of automotive hose are fuel hose, air conditioning hose, radiator hose, power steering hose, brake hose, turbo charging hose. Of course, the use of these vehicles is different, so for their respective performance requirements are not the same. For example, the power steering hose contact medium is mineral oil, thermal performance is good, the joint part of the firm. In this study, it mainly by the use of chlorinated polyethylene rubber (CM), supplemented by other types of rubber, respectively, to study the plasticizer (DOP), carbon black, accelerator (NA-22), and various types of coupling agent treated calcium carbonate content factors influence on the performance of vulcanized rubber. With the increase of DOP content, the hardness of CM rubber is decreasing. With the increase of the amount of NA-22, the tensile strength of CM rubber has been around 19MPa, and the hardness is increasing. With the increase in the amount of carbon black, the CM rubber tensile strength increased first and then decreased, up to a maximum of 19.52MPa; after aging on the tensile properties of the rubber are on the rise, but reach a certain aging time, the tensile properties decreased; tensile deformation rate and permanent deformation rate all the time with the increasing of aging time decreases. Effect of calcium carbonate treated with titanate coupling agent for rubber properties of the most stable, the most significant effect of aluminium and titanium complex coupling agent.
Keyword: Automotive rubber hose; chlorinated polyethylene rubber (CM); plasticizer; promoter; carbon black; coupling agent.
目 录
1 绪论 1
1.1 汽车胶管概述 1
1.2 汽车胶管的发展历程 2
1.3 橡胶硫化 3
1.4 橡胶硫化体系的组成 4
1.4.1 过氧化物硫化体系 4
1.4.2 硫脲硫化体系 5
1.4.3 噻二唑硫化体系 6
1.5 橡胶硫化机理 7
1.6 汽车胶管的发展趋势 7
1.7 本论文的研究背景、研究意义和研究内容 7
2 实验部分 9
2.1 实验原料 9
2.2 主要仪器及设备
-
不同链长聚二甲基硅氧烷...
-
电弧离子镀TiAlN硬质薄膜的制备及性能研究
-
电弧离子镀TiCN硬质薄膜的制备及性能研究
-
稀土元素Dy对合金涂层结构与高温性能的影响
-
金属纳米晶体铁磁转变温度的热力学研究
-
热管/超声协同FSW弱连接的...
-
ZK60表面MAO-ED陶瓷/HA复合生物涂层的制备
浅析中国古代宗法制度
江苏省某高中学生体质现状的调查研究
上市公司股权结构对经营绩效的影响研究
巴金《激流三部曲》高觉新的悲剧命运
中国传统元素在游戏角色...
现代简约美式风格在室内家装中的运用
NFC协议物理层的软件实现+文献综述
C++最短路径算法研究和程序设计
高警觉工作人群的元情绪...
g-C3N4光催化剂的制备和光催化性能研究