摘要：TWIP钢中Mn含量高，其合金化是生产过程中一个很大的技术难点，为了提高Mn的回收率，采用低廉的碳的氧化来取代锰的氧化“去碳保锰”。但去碳保锰所需最低温度或同温度下的最低碳含量与去碳保锰反应中氧化锰的活度有关。而渣的碱度对MnO的活度有重要的影响。本研究采用化学平衡法研究液体Ag与CaO-SiO2-MnO-FeO-MgO系熔渣间的反应平衡，获得液体Ag中的平衡Mn含量及与之平衡的渣中各组分的浓度，从而获得TWIP钢的熔炼过程中熔渣中MnO的活度。特别是渣中碱度对MnO活度的影响。结果表明：（1）渣中MnO的活度系数基本随着渣中碱度的增加而增加。61924

（2）渣中MnO的活度随着碱度的提高而显著地提高。

（3）渣中MnO的活度系数与碱度间的关系为：

毕业论文关键词： 熔渣；碱度；MnO；活度系数；活度

Study on the effect of basicity on the activity of MnO in slag

Abstract：Mn content and alloying of TWIP steel is a great technical difficulty in the production process，in order to improve the recovery rate of Mn， the use of low carbon oxidation to replace the manganese oxide，and to carbon and manganese.However，it is related to the lowest carbon content and the activity of manganese oxide in the reaction of carbon and manganese to protect the minimum temperature or the same temperature.And the presence of CaO in the slag has an important influence on the activity of MnO.Therefore，the activity of the slag melting process of the chemical balance method of TWIP steel in MnO.In particular，the effect of CaO and the ratio of slag on the activity of MnO.（1) under different MnO content，the equilibrium concentrations of Mn of slag and gold are usually different，the activity coefficient of MnO in slag is increased with the increase of the content of alkalinity in slag(2) the activity of MnO in the slag was significantly increased with the increase of basicity.(3)the relationship between the activity coefficient of MnO and the basicity of the slag can be: 

Key  words: slag；alkalinity；MnO；activity coefficient；activity

目录

1  绪论 1

1.1  TWIP钢简介 1

1.1.1  TWIP钢的研究现状 1

1.1.2  TWIP钢的结构与显微组织、组织性能 1

1.1.3  TWIP钢的成分与合金元素的作用 3

1.1.4  TWIP钢的力学性能 3

1.2  活度、活度系数和活度相互作用系数 5

1.2.1  活度、活度系数和活度相互作用系数 5

1.2.2  活度和活度系数 5

1.2.3  活度相互作用系数 6

1.3  活度的测量方法 7

1.3.1  化学平衡法 7

1.3.2  固体电解质法 8

1.3.3  蒸气压法 10

1.3.4  三元相图法 11

2  本次研究的目的和内容 13

2.1  课题研究的意义 13

2.2  课题研究的内容 13

3  实验研究方法 14

3.1  实验研究原理 14

3.2  实验设备和原材料 14