摘要FeSiCuNbB 纳米晶软磁合金是具有较高的磁导率和较低的磁滞损耗等优点，凭借其优异的软磁性能很快得到了应用，成为了目前电力电子行业广泛采用的新型磁性材料之一。

本文利用DSC、XRD和VSM等研究了微波退火工艺对FeSiCuNbB非晶带材晶化过程和性能的影响。研究发现，FeSiCuNbB快淬薄带淬态组织以非晶相为主，具有较好的非晶形成能力。合金非晶晶化过程存在两个阶段, 分别对应于α-Fe(Si)相和Fe3B 相析出, 其晶化激活能分别为125。084 kJ/mol和249。6790 kJ/mol。适当的微波退火工艺对铁基非晶合金材料的软磁性能有显著的提高，非晶薄带在2000 W微波功率下退火12 min获得最佳磁性能。80538

毕业论文关键词：铁基非晶合金；软磁性能；微波退火

Abstract FeSiCuNbB nanocrystalline soft magnetic alloy has the advantages of high permeability and low hysteresis loss, and has been widely used by the excellent soft magnetic properties, which is one of the new magnetic materials widely used in the power electronics industry。

In this paper, the effects of microwave annealing on the crystallization process and properties of FeSiCuNbB amorphous strip were studied by DSC, XRD and VSM。 It is found that the quench state of FeSiCuNbB is characterized by amorphous phase, and has good amorphous forming ability。 The amorphization process of alloy has two stages, which correspond to α-Fe (Si) phase and Fe3B phase precipitation, and its crystallization activation energy is 125。084 kJ / mol and 249。6790 kJ / mol, respectively。 The microwave annealing process has a significant improvement in the soft magnetic properties of Fe-based amorphous alloy materials, and the amorphous strip is annealed at 2000W for 12 min to obtain the best magnetic properties。

Keywords: iron-based amorphous alloy；Soft magnetic properties；Microwave annealing

目录

1。 绪论 1

1。1 引言 1

1。2 铁基非晶合金的发展概况 2

1。3 非晶合金的形成原理与制备 2

1。4 铁基非晶晶化原理 3

1。5 微波退火工艺研究 3

1。6 铁基非晶/纳米晶合金的性能与应用 4

1。6。1 软磁性 4

1。6。2 力学性能 5

1。6。3 铁基非晶合金应用领域 5

1。7 研究意义和主要内容 6

2。 实验内容 7

2。1 实验过程 7

2。1。1 试样的制备和实验流程 7

2。1。2 DSC测试 8

2。1。3 XRD测试 8

2。1。4 VSM测试 8

2。1。5 真空封装处理 9

2。1。6 退火处理 9

2。2 实验仪器和设备 9

2。2。1 实验仪器 9

2。2。2 实验设备 9

2。3 实验仪器和设备简介 10

2。3。1 高温差热分析仪 10

2。3。2 X-射线衍射 11

2。3。3 振动样品磁强计（VSM） 12

2。4 实验分组