摘要:卟啉在乙醇中超声分散与钨酸铋杂化形成卟啉/钨酸铋复合材料。卟啉分子作为增敏剂主要通过共轭作用附着在钨酸铋薄片上。可见光照射下卟啉/钨酸铋复合材料苯酚的降解上显示较高的光催化活性，本实验通过掺杂不同比例的卟啉以制备卟啉/钨酸铋复合材料，利用罗丹明-B污染物的降解来评价光催化材料的性能。分别比较不同复合比例的光催化材料的光催化活性高低，同时用XRD衍射仪、透射电镜表征其微观形貌、结构，并与参考文献中结果相对照，研究卟啉/钨酸铋光催化材料的光催化机理，总结制备高活性卟啉/钨酸铋光催化材料的方法和条件80748

毕业论文关键词：钨酸铋；卟啉；光催化分解

research of photocatalytic properties of CuTCPP/Bi2WO6

Abstract：Porphyrin / bismuth tungstate hybrid materials were synthesied by ultrasonic dispered in ethanol。 The porphyrin molecule as sensitier is attached to bismuth tungstate thin sheet by the conjugation effect。 The photocatalysis activity of porphyrin / bismuth composite was observed under visible light irradiation。 the porphyrin / bismuth tungstate composite was prepared by doping different ratios of porphyrin to prepare porphyrin / Tungstic acid composite materials, and the degradation of photocatalytic material was evaluated by the degradation of RhB。 The photocatalytic activity of different composite proportion of photocatalysis materials was compared, and the morphology and structure of the photocatalysis materials were characteried by XRD and tem。 We discuss the photocatalyysis mechanism of porphyrin / bismuth photocatalysis, and the method and conditions of preparing high activity porphyrin / Tungstic tungstate photocatalytion material。

Keywords: Bi2WO6；porphyrin，Photocatalytion degradation

目录

摘要 II

关键词 II

Abstract II

Keywords II

1 绪论 1

1。1 研究背景 1

1。2 研究的目的与内容 1

1。3 半导体光催化原理 2

1。4 半导体光催化影响因素 4

1。4。1 晶相结构 4

1。4。2 结晶度与表面态 4

1。4。3 晶粒尺寸与表面积 4

1。4。4 光催化反应条件 5

1。5 增强半导体光催化性能的方法 6

1。5。1 元素掺杂 6

1。5。2 形成固溶体 7

1。5。3半导体复合 7

1。5。4 有机染料光敏化 7

1。5。5 碳类材料复合 8

2 实验部分 9

2。1 原料简介 9

2。1。1 钨酸铋 9

2。1。2 卟啉 10

2。2 样品制备方法 10

2。2。1 热液法 10

2。2。2 共沉淀法 11

2。2。3 超声分散法 11

2。2。4 固相烧结法 12

2。2。5 模板法