摘要：导电聚合物由于其较低的热导率和较高的电导率理论上具备了作为热电材料的潜力，同时由于其热导率低、资源丰富、价格低廉等优点而备受关注。聚苯胺是目前研究较多的导电聚合物之一，聚苯胺基复合材料的热电性能也有了较大的提高。本文采用FeCl3 作为氧化剂与掺杂剂，通过原位聚合法制备了导电炭黑/聚苯胺的复合热电材料，并运用扫描电镜、拉曼光谱、X射线光电子能谱、透射电镜等对导电炭黑/聚苯胺复合材料的组成和微观结构进行了研究。同时通过测试复合材料的电导率，主要研究了导电炭黑含量对导电炭黑/聚苯胺复合材料电导率的影响，并与机械混合法所制备的导电炭黑/聚苯胺复合材料的性能进行了对比。81024

毕业论文关键词：聚苯胺；导电炭黑；复合材料；原位聚合法；热电性能

Preparation of thermoelectric properties of conductive carbon black/polyaniline composite materials 

Abstract: Conductive polymer has a great potential to be used as a thermoelectric material due to its low thermal conductivity, low prices, and abundant resources。 Polyaniline (PANI) is one of the most studied conductive polymers, and the thermoelectric properties of PANI based composite materials have been greatly enhanced。 Herein, conductive carbon black (CB)/PANI thermoelectric composite materials were prepared via an in-situ polymerization method using FeCl3 as oxidant and dopant。 The composition and morphology of the CB/ PANI thermoelectric composite materials were investigated by scanning electron microscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy。 The influence of CB content on the electrical conductivity of CB/ PANI composites was investigated。 The results were also compared with that of the CB/ PANI composites prepared by a mechanical mixing method。

Key Words: Polyaniline; Conductive carbon black; Composite materials; In-situ polymerization; Thermoelectric properties

目录

1 文献综述 1

1。1 热电材料 1

1。2 聚苯胺热电材料的研究进展 2

1。2。1 聚苯胺简介 2

1。2。2 聚苯胺的合成 3

1。2。3 聚苯胺热电材料的研究进展 4

1。3 聚苯胺复合热电材料的研究进展 5

1。3。1 碳纳米管/聚苯胺复合热电材料 6

1。3。2 石墨烯/聚苯胺复合热电材料 6

1。3。3 炭黑/聚苯胺复合热电材料 7

1。4 本课题的提出以及研究意义 8

2 实验部分 10

2。1 实验原材料 10

2。2 实验所需合成设备 10

2。3 原位聚合制备聚苯胺/导电炭黑复合热电材料 10

2。3。1实验配方 11

2。3。2 原位聚合法制备具体流程 11

2。4。 机械混合法制备炭黑/聚苯胺复合热电材料 14

2。5 实验表征和测试设备 15

2。5。1 XPS 15

2。5。2 拉曼光谱 16

2。5。3 SEM 16

2。5。4 TEM