摘要前人研究表明将碱金属碳酸盐/碳酸氢盐负载到多孔材料催化剂将提升了碱金属碳酸盐与CO2的反应活性，降低了反应产物的再生活化能。借鉴上述研究思路，本文选用TiO2、TiO(OH)2、ZrO2、钛酸丁酯四种多孔载体材料作为掺杂剂，并以5%的量混合配比为1:1:1的TEOS/APTES/Na2CO3，制备新型的复合型钠基吸收剂。本文利用自行搭建的小型固定床试验台进行实验，并用SEM 和氮吸附仪进行表征，详细分析TiO2等掺杂剂对钠基吸收剂碳酸化反应特性的宏观和微观的影响。结果表明，添加掺杂剂的复合型钠基吸收剂的脱碳能力提高，脱碳量增加了近28%，同时掺杂剂使得吸收剂碳酸化反应速率有所提高。87664

毕业论文关键词  CO2捕集  复合型钠基吸收剂  掺杂剂  催化脱碳  超临界干燥

毕业设计说明书外文摘要

Title    Study on the catalytic mechanism of compound sodium  decarburization absorbent                               

Abstract Previous studies showed that the alkali metal carbonate / bicarbonate load to the catalyst of porous materials will enhance the alkali metal carbonate and CO2 reactivity and decrease the activation energy of the reaction product of regeneration。 Referring to the research ideas, this paper selects TiO2, TiO (OH)2, ZrO2 and tetrabutyl titanate four porous carrier material as the dopant, and with 5% volume mixing ratio is 1:1:1 TEOS/APTES/Na2CO3 prepared new compound sodium based sorbents。 The self built small fixed bed test rig experiments, and were characterized by SEM and nitrogen adsorption instrument, detailed analysis of TiO2 dopant on sodium based sorbent carbonation reaction characteristics of macroscopic and microscopic。 The results show that the dopant compound sodium based sorbents decarburization capacity addition to increase, the amount of decarbonization increased nearly 28% and the dopant the carbonation reaction rate increased。From+优|尔-论_文W网wWw.YouErw.com 加QQ752018.766

Keywords  CO2 capture  compound sodium based sorbent  dopant  catalytic decarbonization  supercritical drying method

目录

1  绪论 1

1。1  课题研究背景及意义 1

1。2  碱金属基固体CO2吸收剂研究进展 2

1。3  氨基修饰的固体吸收剂研究进展 4

1。4  本文的研究目的和技术方案 5

1。5  本章小结 7

2  实验原理、方法及误差分析 8

2。1  复合型钠基吸收剂吸收 CO2的基本原理与计算方法 8

2。2  复合型钠基吸收剂的制备 9

2。3  吸收剂碳酸化/再生测试实验系统和方法 11

2。4  表征方法 15

2。5  实验误差分析 16

2。6  本章小结 18

3  配比的筛选 19

3。1  载体的确定 19

3。2  活性成分的确定 22

3。3  干燥方式的确定 23

3。4  配比的筛选 24

3。5  本章小结