摘要：纤维素作为自然界中含量最丰富的生物质组分，将其通过绿色高效的手段水解为可溶性的还原糖是合理有效利用纤维素的关键。针对传统研究采用的催化剂存在腐蚀性较大、作用条件苛刻、不易回收、对环境污染大等不足，本文以纤维素为原料，选用具有不腐蚀设备、易于回收利用、对环境友好、稳定性好和活性高等优点的新型磁性仿酶树脂固体酸为催化剂，在离子液体1-丁基-3-甲基咪唑氯盐中研究对纤维素的水解效果，并考察各种反应条件对纤维素水解效果的影响。研究结果表明：在[BMIM]Cl用量为2g，水的用量为10µL，纤维素用量为50mg，催化剂MCMPS-1-SO3H-21用量为30mg，反应温度为130°C，反应时间为120min，还原糖的最大产率可以达到49。16%。91661

毕业论文关键字：纤维素，水解，还原糖，树脂固体酸，离子液体

Abstract: As the most abundant component in nature, the hydrolysis of cellulose into the soluble reducing sugars by means of green and efficient methods is the key to use it reasonably and efficiently。 According to the current research situations and existing problems such as more corrosive, harsh operating conditions, difficult to recycle and great environmental pollution, magnetic cellulase-mimetic resin catalyst (MCMPS-1-SO3H-21) with various  excellent properties was used for the hydrolysis of cellulose into reducing sugars。 The results indicated that the highest yield of total reducing sugars with 49。16% was achieved under the following reaction conditions: 2 g [BMIM]Cl, 10 µL H2O, 50 mg cellulose, 30 mg MCMPS-1-SO3H-21, 130 °C, 120 min。

Keyword: Cellulose, hydrolysis, reducing sugar, resin solid acid, ionic liquid

目录

1 前言 4

1。1 纤维素 4

1。2 纤维素水解的研究进展 4

1。3 选题背景及意义 6

2 材料与方法 6

2。1 实验试剂及仪器 6

2。2 磁性仿酶树脂固体酸催化剂MCMPS-SO3H的制备 7

2。3 碳基固体酸催化剂的表征 8

2。4 纤维素的水解反应 8

2。5 还原糖的测定 8

2。6 紫外法测定HMF 10

3 结果与讨论 11

3。1 催化剂的表征结果 11

3。2 不同催化剂催化活性的比较 12

3。3 不同反应温度对纤维素水解的影响 13

3。4 不同反应时间对纤维素水解的影响 14

3。5 不同催化剂用量对纤维素水解的影响 16

3。6 不同水分含量对纤维素水解的影响 17